Crack initiation on 316L(N) CT specimens under creep-fatigue conditions

被引：0
|
作者：
Laiarinandrasana, L [1 ]
Piques, R [1 ]
Drubay, B [1 ]
Faidy, C [1 ]
机构：
[1] URA CNRS 866, EMP, F-91003 Evry, France
来源：
LIFE ASSESSMENT AND LIFE EXTENSION OF ENGINEERING PLANT, STRUCTURES AND COMPONENTS | 1996年
关键词：
D O I：
暂无
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In power plant operating at elevated temperatures, components are subjected to complex loading history including creep, fatigue and creep-fatigue effects. A practical and validated method for calculating the initiation time for pre-existing defects is needed. An attempt is made to analyze creep-fatigue tests performed at both the Ecole des Mines de Paris (EMP) and the Commissariat a l'Energie Atomique (CEA) Saclay on 316L(N) CT specimens, by combining local and global approaches on crack initiation with Fracture Mechanics concepts.
引用
收藏
页码：95 / 102
页数：8
相关论文
共 50 条
  • [21] CREEP-FATIGUE BEHAVIOR AND LIFE PREDICTION OF 316L STAINLESS STEEL UNDER DIFFERENT LOADING LEVELS
    Jiang, Huifeng
    Chen, Xuedong
    Fan, Zhichao
    Dong, Jie
    Jiang, Heng
    PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, VOL 6, PTS A AND B, 2010, : 1445 - 1450
  • [22] Fatigue crack initiation and crystallographic growth in 316L stainless steel
    Sistaninia, M.
    Niffenegger, M.
    INTERNATIONAL JOURNAL OF FATIGUE, 2015, 70 : 163 - 170
  • [23] Crack initiation, propagation, and arrest in 316L model pipe components under thermal fatigue
    Paffumi, E
    Nilsson, KF
    Taylor, N
    Hurst, R
    Bache, M
    Fatigue and Fracture Mechanics, 34th Volume, 2005, (1461): : 539 - 556
  • [24] EFFECT OF CREEP FRACTURE TOUGHNESS ON CRACK INITIATION AND PROPAGATION UNDER CREEP-FATIGUE INTERACTION.
    Zhou, Shunshen
    Jinshu Xuebao/Acta Metallurgica Sinica, 1987, 23 (03):
  • [25] Characterization of low-cycle fatigue and creep-fatigue induced damage in a 316L stainless steel
    Simon, Sergio
    Rodriguez Ibabe, Jose M.
    Fuentes, Manuel
    Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques, 1994, 85 (04): : 273 - 281
  • [26] Crack behaviour of 10Cr-steels under creep and creep-fatigue conditions
    Mueller, F.
    Scholz, A.
    Berger, C.
    Klenk, A.
    Maile, K.
    Roos, E.
    MATERIALS AT HIGH TEMPERATURES, 2008, 25 (03) : 169 - 178
  • [27] Specimen geometry effect on creep crack growth in 316L(N)
    Laiarinandrasana, L
    Kabiri, R
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2006, 29 (02) : 145 - 155
  • [28] A practical method based on stress evaluation (sigma(d) criterion) to predict initiation of crack under creep and creep-fatigue conditions
    Moulin, D
    Drubay, B
    Acker, D
    Laiarinandrasana, L
    JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 1995, 117 (04): : 335 - 340
  • [29] FATIGUE CRACK INITIATION AND GROWTH IN 316L STEEL IN TORSIONAL CYCLIC LOADING
    Karol', M.
    Chlupova, A.
    Mazanova, V.
    Kruml, T.
    ENGINEERING MECHANICS 2017, 2017, : 434 - 437
  • [30] Evaluation of the creep-fatigue damage mechanism of Type 316L and Type 316LN stainless steel
    Kim, Dae Whan
    Chang, Jong-Hwa
    Ryu, Woo-Seog
    INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2008, 85 (06) : 378 - 384
12345