Effect of electron beam irradiation on compatibility of HDPE/PA6 blend

被引：4

作者：

Lian, TJ ^{[1
]}

Xu, W ^{[1
]}

Liu, PB ^{[1
]}

Ren, HS ^{[1
]}

机构：

[1] Sichuan Univ, State Key Lab Polymer Mat Engn China, Polymer Res Inst, Chengdu 610065, Peoples R China

来源：

POLYMER-PLASTICS TECHNOLOGY AND ENGINEERING | 2004年 / 43卷 / 01期

关键词：

electron bean; irradiation; high-density polyethylene; polyamide; 6; compatibility;

D O I：

10.1081/PPT-120027462

中图分类号：

O63 [高分子化学（高聚物）];

学科分类号：

070305 ; 080501 ; 081704 ;

摘要：

The compatibility of polyamide (PA6) and the electron beam irradiated high density polyethylene (e-HDPE) was studied in this paper. Some oxygen-containing groups (mainly the carbonyl group) are introduced into the molecular chains of HDPE through electron beam irradiation, thus the polarity of HDPE is increased, and the surface tension of HDPE increased from 32.47 dyne/cm to 36.05 dyne/cm, especially the hydrogen bond part of the surface tension, which was increased from 1.21 dyne/cm to 1.74 dyne/cm. It shows that through electron beam irradiation, the ability of the irradiated HDPE to form hydrogen bonds with the polar groups of the PA6 was improved, and the mechanical properties of the HDPE/PA6 blend was also improved.

引用

页码：31 / 40

页数：10

共 8 条

[1]

Abou Zeid HM, 2000, J APPL POLYM SCI, V75, P179, DOI 10.1002/(SICI)1097-4628(20000110)75:2<179::AID-APP1>3.0.CO

[2]

2-B

[3]

IVANOV VS, 1992, RAD CHEM POLYM, P191

[4]

Kitazaki Y., 1972, J ADHES SOC JPN, V8, P131