Aging behavior of the Ti-29Nb-13Ta-4.6Zr new beta alloy for medical implants

被引：69
作者：
Ikeda, M [1 ]
Komatsu, SY
Sowa, I
Niinomi, M
机构：
[1] Kansai Univ, Fac Engn, Dept Mat Sci & Engn, Osaka 5648680, Japan
[2] Toyohashi Univ Technol, Dept Prod Syst Engn, Toyohashi, Aichi 4418580, Japan
[3] Kyoei Steel Ltd, Osaka 5300004, Japan
来源：
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE | 2002年 / 33卷 / 03期
关键词：
D O I：
10.1007/s11661-002-0110-9
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The aging behavior of the Ti-29Nb-13Ta-4.6Zr alloy quenched from 1033 K was investigated by employing electrical resistivity (rho) and Vickers hardness (HV) measurements, optical microscopy (OM), and X-ray diffraction (XRD). Upon aging at 573 K, the rho value at room- and liquid-nitrogen temperatures initially increased to 120 and 30 ks, respectively, and decreased with continued aging time. The HV value started to increase from 0.06 ks and the isothermal omega phase was identified at 300 ks of aging by XRD. On aging at 773 K, an incubation period of 6 ks was observed for the rho change at both temperatures, following which rho decreased. An incubation period for the HV change was extended up to 12 ks, and then HV increased. Precipitated alpha was observed and identified by OM and XRD, respectively, whereas no reflections of isothermal omega phase were identified during the whole aging time at 773 K. The upper-limit temperature of isothermal omega precipitation is situated at around 673 K.
引用
收藏
页码：487 / 493
页数：7
相关论文
共 39 条
  • [1] Ahmed T., 1996, TITANIUM 95 SCI TECH, P1760
  • [2] FORMATION OF OMEGA- PHASE IN TI-NB ALLOYS
    BALCERZAK, AT
    SASS, SL
    [J]. METALLURGICAL TRANSACTIONS, 1972, 3 (06): : 1601 - +
  • [3] BANIA PJ, 1993, BETA TITANIUM ALLOYS IN THE 1990S, P3
  • [4] Bania PJ, 1984, BETA TITANIUM ALLOYS, P209
  • [5] BLACKBURN MJ, 1968, T METALL SOC AIME, V242, P2461
  • [6] Boyer R.R., 1984, BETA TITANIUM ALLOYS, P441
  • [7] DETERMINATION OF OMEGA PHASE MORPHOLOGY IN TI-35 PER CENT NB BY TRANSMISSION ELECTRON MICROSCOPY
    BRAMMER, WG
    RHODES, CG
    [J]. PHILOSOPHICAL MAGAZINE, 1967, 16 (141): : 477 - &
  • [8] BROTZEN FR, 1955, T AM I MIN MET ENG, V203, P413
  • [9] INFLUENCE OF CONSTITUTION AND MICROSTRUCTURE ON TEMPERATURE-COEFFICIENT OF RESISTIVITY IN TI-BASE ALLOYS
    CHANDRASEKARAN, V
    TAGGART, R
    POLONIS, DH
    [J]. JOURNAL OF MATERIALS SCIENCE, 1974, 9 (06) : 961 - 968
  • [10] Chandrasekaran V., 1972, Metallography, V5, P393, DOI 10.1016/0026-0800(72)90027-4
1234