Comparative Studies on Microstructure, Mechanical and Pitting Corrosion of Post Weld Heat Treated IN718 Superalloy GTA and EB Welds
被引:0
作者:
Dilkush
[1
]
Mohammed, Raffi
[2
]
Reddy, G. Madhusudhan
[4
]
Rao, K. Srinivasa
[3
]
机构:
[1] RGUKT, Dept Met & Mat Engn, Nuzvid, India
[2] NIT Andhra Pradesh, Dept Met & Mat Engn, Tadepalligudem, Andhra Pradesh, India
[3] Andhra Univ, Dept Met Engn, Visakhapatnam, Andhra Pradesh, India
[4] Def Met Res Lab, Hyderabad, Telangana, India
来源:
INTERNATIONAL CONFERENCE ON RECENT ADVANCES IN MATERIALS, MECHANICAL AND CIVIL ENGINEERING
|
2018年
/
330卷
关键词:
PRECIPITATION;
CRACKING;
SOLIDIFICATION;
BEHAVIOR;
D O I:
10.1088/1757-899X/330/1/012051
中图分类号:
TU [建筑科学];
学科分类号:
0813 ;
摘要:
In the present study, an attempt has been made to weld Inconel 718 nickel-base superalloy (IN718 alloy) using gas tungsten arc welding (GTAW) and electron beam welding (EBW) processes. Both the weldments were subjected to post-weld heat treatment condition as follows -980(0)C /20 min followed by direct aging condition (DA) as 720(0)C/8 h/FC followed by 620(0)C /8 h/AC. The GTA and EB welds of IN718 alloy were compared in two conditions as-received and 980STA conditions. Welds were characterized to observe mechanical properties, pitting corrosion resistance by correlating with observed microstructures. The rate of higher cooling ranges, the fusion zone of EBW exhibited discrete and relative finer lave phases whereas the higher niobium existed laves with coarser structure were observed in GTAW. The significant dissolution of laves were observed at 980STA of EBW. Due to these effects, the EBW of IN718 alloy showed the higher mechanical properties than GTAW. The electrochemical potentiostatic etch test was carried out in 3.5wt% sodium chloride (NaCl) solution to study the pitting corrosion behaviour of the welds. Results of the present investigation established that mechanical properties and pitting corrosion behaviour are significantly better in post weld heat treated condition. The comparative studies showed that the better combination of mechanical properties and pitting corrosion resistance were obtained in 980STA condition of EBW than GTAW.