Structural Transformations in Austenitic Stainless Steel Induced by Deuterium Implantation: Irradiation at 295 K

被引:1
作者
Morozov, Oleksandr [1 ]
Zhurba, Volodymir [1 ]
Neklyudov, Ivan [1 ]
Mats, Oleksandr [1 ]
Progolaieva, Viktoria [1 ]
Boshko, Valerian [1 ]
机构
[1] Kharkiv Inst Phys & Technol, Natl Sci Ctr, 1 Akad St, UA-61108 Kharkov, Ukraine
来源
NANOSCALE RESEARCH LETTERS | 2016年 / 11卷
关键词
Structural transformations; Austenitic stainless steel; Deuterium; Ion implantation; Irradiation at 295 K; TDS; TEM; HYDROGEN EMBRITTLEMENT; CRACK-GROWTH; MARTENSITE; ALLOYS; PHASE; 304-STAINLESS-STEEL; DIFFRACTION; RETENTION; DEFECTS; FATIGUE;
D O I
10.1186/s11671-016-1251-x
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
Deuterium thermal desorption spectra were investigated on the samples of austenitic steel 18Cr10NiTi pre-implanted at 295 K with deuterium ions in the dose range from 8 x 10(14) to 2.7 x 10(18) D/cm(2). The kinetics of structural transformation development in the steel layer was traced from deuterium thermodesorption spectra as a function of deuterium concentration. Three characteristic regions with different low rates of deuterium amount desorption as the implantation dose increases were revealed: I-the linear region of low implantation doses (up to 1 x 10(17) D/cm(2)); II-the nonlinear region of medium implantation doses (1 x 10(17) to 8 x 10(17) D/cm(2)); III-the linear region of high implantation doses (8 x 10(17) to 2.7 x 10(18) D/cm(2)). During the process of deuterium ion irradiation, the coefficient of deuterium retention in steel varies in discrete steps. Each of the discrete regions of deuterium retention coefficient variation corresponds to different implanted-matter states formed during deuterium ion implantation. The low-dose region is characterized by formation of deuterium-vacancy complexes and solid-solution phase state of deuterium in the steel. The total concentration of the accumulated deuterium in this region varies between 2.5 and 3 at.%. The medium-dose region is characterized by the radiation-induced action on the steel in the presence of deuterium with the resulting formation of the energy-stable nanosized crystalline structure of steel, having a developed network of intercrystalline boundaries. The basis for this developed network of intercrystalline boundaries is provided by the amorphous state, which manifests itself in the thermodesorption spectra as a widely temperature-scale extended region of deuterium desorption (structure formation with a varying activation energy). The total concentration of the accumulated deuterium in the region of medium implantation doses makes 7 to 8 at.%. The resulting structure shows stability against the action of deuterium ion implantation. This manifests itself in a nearly complete ceasing of deuterium accumulation from a newly implanted dose (radiation-resistant structure).
引用
收藏
页码:1 / 13
页数:13
相关论文
共 50 条
[41]   Influence of Si on strain-induced martensitic transformation in metastable austenitic stainless steel [J].
Li, Yaji ;
Li, Jun ;
Ma, Jinyao ;
Han, Peide .
MATERIALS TODAY COMMUNICATIONS, 2022, 31
[42]   Effect of reversion of strain induced martensite on microstructure and mechanical properties in an austenitic stainless steel [J].
S. K. Ghosh ;
P. Mallick ;
P. P. Chattopadhyay .
Journal of Materials Science, 2011, 46 :3480-3487
[43]   Film-induced stress enhancing stress corrosion cracking of austenitic stainless steel [J].
李金许 ;
陈浩 ;
王燕斌 ;
乔利杰 ;
褚武扬 .
Science in China(Series E:Technological Sciences), 2001, (06) :581-589
[44]   Film-induced stress enhancing stress corrosion cracking of austenitic stainless steel [J].
Li, JX ;
Chen, H ;
Wang, YB ;
Qiao, LJ ;
Chu, WY .
SCIENCE IN CHINA SERIES E-TECHNOLOGICAL SCIENCES, 2001, 44 (06) :581-589
[45]   Medium-temperature plasma immersion-ion implantation of austenitic stainless steel [J].
Tian, XB ;
Zeng, ZM ;
Zhang, T ;
Tang, BY ;
Chu, PK .
THIN SOLID FILMS, 2000, 366 (1-2) :150-154
[46]   Role of irradiation and irradiation defects on the oxidation first stages of a 316L austenitic stainless steel [J].
Boisson, M. ;
Legras, L. ;
Andrieu, E. ;
Laffont, L. .
CORROSION SCIENCE, 2019, 161
[47]   Formation of abnormally thick amorphous layer in austenitic stainless steel by nitrogen ion implantation [J].
Li, X ;
Samandi, M ;
Dunne, D .
METASTABLE, MECHANICALLY ALLOYED AND NANOCRYSTALLINE MATERIALS, PTS 1 AND 2, 1996, 225 :179-184
[48]   Crystallographic analysis of Ga plus irradiation-induced phase transformation in austenitic stainless steels [J].
Shimizu, Kazuyuki ;
Tsuruta, Hanako ;
Kamada, Yasuhiro ;
Murakami, Takeshi ;
Watanabe, Hideo .
MATERIALS CHARACTERIZATION, 2022, 194
[49]   Transpassivation-induced structural evolution of oxide film on 654SMO super austenitic stainless steel [J].
Wei, X. X. ;
Zhang, B. ;
Xu, Y. T. ;
Chen, Z. Y. ;
Li, X. L. ;
Ma, X. L. .
CORROSION SCIENCE, 2024, 232
[50]   Unraveling indentation-induced slip steps in austenitic stainless steel [J].
Xia, Wenzhen ;
Dehm, Gerhard ;
Brinckmann, Steffen .
MATERIALS & DESIGN, 2019, 183