Optimization of shielding gas composition in high nitrogen stainless steel gas metal arc welding

被引:16
作者
Liu, Zeng [1 ]
Fan, Chenglei [1 ]
Ming, Zhu [2 ,3 ]
Chen, Chao [1 ]
Yang, Chunli [1 ]
Lin, Sanbao [1 ]
Wang, Langping [1 ]
机构
[1] Harbin Inst Technol, State Key Lab Adv Welding & Joining, 912,92 Xidazhi St, Harbin 150001, Peoples R China
[2] Inner Mongolia Met Mat Res Inst, Ningbo, Peoples R China
[3] Nanjing Univ Sci & Technol, Sch Mat Sci & Engn, Nanjing, Jiangsu, Peoples R China
关键词
High nitrogen stainless steel filler metal; Ar-N-2-CO2 shielding gas; Mechanical properties optimization; PITTING CORROSION; MICROSTRUCTURE; WELDABILITY; TUNGSTEN; AR-O-2; ZONE; FLUX;
D O I
10.1016/j.jmapro.2020.08.001
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
High nitrogen stainless steel has extensive applied foreground in industries. But the weldability limits the use of the steel. The weld without nitrogen can become the weakness of the joint in corrosion resistance and strength. In this study, response surface methodology was applied to optimize the Ar-N-2-CO2 ternary shielding gas for a nitrogen-containing filler metal in high nitrogen stainless welding. The influence of the proportion of N-2 and CO2 on the nitrogen content, the impact energy and the tensile strength were investigated by the statistical regression models. The results show that the tensile strength, nitrogen content and impact energy increase and then decrease with the increasing of CO2, which indicates that CO2 content should not be too high. N-2 addition can increase the nitrogen content of the weld obviously. But the impact energy decreases when N-2 content exceeds about 7%. Integrating the mathematic models of the three performances, the optimal shielding gas compositions were determined to be 87 %Ar-6.5 %N-2-6.5 %CO2. With this optimal shielding gas, the tensile strength and impact energy reached 956.7 MPa and 166.8 J, respectively. The deviation between the experimental value and the predicted value was below 2%.
引用
收藏
页码:19 / 29
页数:11
相关论文
共 30 条
[1]   Manufacture and application of high nitrogen steels [J].
Berns, H .
ISIJ INTERNATIONAL, 1996, 36 (07) :909-914
[2]   Optimization of shielding gas composition in narrow gap GMA welding based on response surface methodology [J].
Cai, Xiaoyu ;
Fan, Chenglei ;
Lin, Sanbao ;
Ji, Xiangru ;
Yang, Chunli .
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2018, 95 (5-8) :2405-2412
[3]  
du Plessis J, 2007, WELD J, V86, p273S
[4]  
Girish J, 2015, INT J SCI RES, V4, P987
[5]   Effects of Cr2N on the pitting corrosion of high nitrogen stainless steels [J].
Ha, HeonYoung ;
Kwon, HyukSang .
ELECTROCHIMICA ACTA, 2007, 52 (05) :2175-2180
[6]   Effects of processing and manufacturing of high nitrogen-containing stainless steels on their mechanical, corrosion and wear properties [J].
Hänninen, H ;
Romu, J ;
Ilola, R ;
Tervo, J ;
Laitinen, A .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2001, 117 (03) :424-430
[7]   Welding of high nitrogen steels [J].
Harzenmoser, M .
MATERIALS AND MANUFACTURING PROCESSES, 2004, 19 (01) :75-86
[8]   Microporosity formation in partially melted zone during welding of high nitrogen austenitic stainless steels [J].
Kamiya, O ;
Chen, ZW ;
Kikuchi, Y .
JOURNAL OF MATERIALS SCIENCE, 2002, 37 (12) :2475-2481
[9]   The development of nitrogen functionality in model chars during gasification in CO2 and O2 [J].
Kapteijn, F ;
Moulijn, JA ;
Matzner, S ;
Boehm, HP .
CARBON, 1999, 37 (07) :1143-1150
[10]   Fabrication of high strength high nitrogen stainless steel with excellent corrosion resistance and its mechanical properties [J].
Katada, Y ;
Sagara, M ;
Kobayashi, Y ;
Kodama, T .
MATERIALS AND MANUFACTURING PROCESSES, 2004, 19 (01) :19-30