Increase the elongation at break of poly (lactic acid) composites for use in food packaging films

Poly (3-hydroxy butyrate) (PHB), cellulose nano crystal (CNC) and a plasticizer (TBC) are mixed together with PLLA with the aim to increase the elongation at break for use in the food packing sector. Spherical (CNC) and fibril nano crystal (CNF) were prepared by hydrolysis of microcrystalline cellulose (MCC) in distilled water, and then stirred using a magnetic stirrer for 15 days and ultrasonic treatment without using any acids as green method. The morphology, thermal, and mechanical properties were studied using POM, DSC, WAXD, SEM and tensile testing, respectively. DSC demonstrated that the addition of PHB, CNC and TBC to PLLA matrix lead to reduce T-g,T-CC and T-m than pure PLLA. FT-IR verified that the carbonyl group C= O appeared broad and some peaks in the PLLA composites 5, 6 and 7 shifted from 3.98 x 10(8) to 4.07 x 10(8) Hz, at 3.54 x 10(8) to 3.44 x 10(8) Hz, at 3.19 x 10(8) to 3.13 x 10(8) Hz. Mechanical testing shows that pure PLLA is brittle, and the elongation at break of PLLA composites reaches up to 205%, making it suitable to use in food packaging.