Effect of crystallisation on electrochemical properties of arc sprayed FeNiCrBSiNbW coatings

被引：13

作者：

Lin, J. R. ^{[1
]}

Wang, Z. H. ^{[1
]}

Lin, P. H. ^{[2
]}

Cheng, J. B. ^{[1
]}

Zhang, X. ^{[1
]}

Hong, S. ^{[1
]}

机构：

[1] Hohai Univ, Coll Mech & Mat, Inst Met & Protect, Nanjing 210098, Jiangsu, Peoples R China

[2] Southeast Univ, Nanjing 211189, Jiangsu, Peoples R China

来源：

SURFACE ENGINEERING | 2014年 / 30卷 / 09期

基金：

中国国家自然科学基金;

关键词：

TWAS; FeNiCrBSiNbW; Corrosion; Annealing; Coating; FE-BASED COATINGS; CORROSION-RESISTANCE; AMORPHOUS COATINGS; BEHAVIOR; ALLOY; WEAR; MICROSTRUCTURE; WC-10CO-4CR; STEEL;

D O I：

10.1179/1743294414Y.0000000299

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

FeNiCrBSiNbW coatings were prepared using a twin wires arc spraying process and were subsequently annealed at 450, 550 and 650 degrees C for 1 h to obtain coatings with different crystallisation. The effect of crystallisation on the electrochemical properties of the coatings was investigated. Transformation of the amorphous phase to crystalline phases of alpha-(Fe, Cr), Fe3B and Fe23B6 occurred when the as sprayed coating was treated at 650 degrees C. Open circuit potential tests, potentiodynamic polarisation tests and electrochemical impendence spectroscopy were employed to investigate the corrosion resistance of the coatings in 3.5 wt-% NaCl solution. The results showed that the corrosion resistance of the coatings decreased with increasing annealing temperature, and the as sprayed coating exhibited the best corrosion resistance among the four kinds of coatings. This was attributed to the high amorphous phase content and the absence of borides such as Fe3B and Fe23B6 phases in the coating.

引用

页码：683 / 687

页数：5

共 28 条

[1]

[Anonymous], 2003, ANN BOOK ASTM STAND

[2]

[Anonymous], 1989, ANN BOOK ASTM STAND

[3] Corrosion behaviour of crystalline and amorphous forms of the glass forming alloy Fe43Cr16Mo16C15B10 [J].

Bakare, M. S. ;

Voisey, K. T. ;

Chokethawai, K. ;

McCartney, D. G. .

JOURNAL OF ALLOYS AND COMPOUNDS, 2012, 527 :210-218

[4] Effects of Crystallization on the Corrosion Resistance of Arc-Sprayed FeBSiNb Coatings [J].

Cheng, J. B. ;

Liang, X. B. ;

Xu, B. S. .

JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2014, 23 (03) :373-379

[5] High-Temperature Erosion Resistance of FeBSiNb Amorphous Coatings Deposited by Arc Spraying for Boiler Applications [J].

Cheng, J. B. ;

Liang, X. B. ;

Chen, Y. X. ;

Wang, Z. H. ;

Xu, B. S. .

JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2013, 22 (05) :820-827

[6] Microstructure and Mechanical Properties of FeBSiNb Metallic Glass Coatings by Twin Wire Arc Spraying [J].

Cheng, J. B. ;

Liang, X. B. ;

Wang, Z. H. ;

Xu, B. S. .

JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2013, 22 (04) :471-477

[7] Wear and Corrosion Behaviors of FeCrBSiNbW Amorphous/Nanocrystalline Coating Prepared by Arc Spraying Process [J].

Cheng, J. B. ;

Wang, Z. H. ;

Xu, B. S. .

JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2012, 21 (05) :1025-1031

[8] The enhancement of the properties of WC-CoHVOF coatings through the use of nanostructured and microstructured feedstock powders [J].

Guilemany, J. M. ;

Dosta, S. ;

Miguel, J. R. .

SURFACE & COATINGS TECHNOLOGY, 2006, 201 (3-4) :1180-1190

[9]

Guo JH, 2007, ACTA METALL SIN, V43, P780

[10] Study of structure and corrosion resistance of Fe-based amorphous coatings prepared by HVAF and HVOF [J].

Guo, R. Q. ;

Zhang, C. ;

Chen, Q. ;

Yang, Y. ;

Li, N. ;

Liu, L. .

CORROSION SCIENCE, 2011, 53 (07) :2351-2356

← 1 2 3 →