A low temperature nitridation route for nanocrystalline AlN

被引:15
作者
Lu, QY
Hu, JQ
Tang, KB [1 ]
Qian, YT
Zhou, G
Liu, XM
Xing, JY
机构
[1] Univ Sci & Technol China, Struct Res Lab, Hefei 230026, Anhui, Peoples R China
[2] Univ Sci & Technol China, Dept Chem, Hefei 230026, Anhui, Peoples R China
关键词
D O I
10.1246/cl.1999.1239
中图分类号
O6 [化学];
学科分类号
0703 ;
摘要
6 nm crystalline A1N has been synthesized through a simple reaction between commercial Al and NH4Cl in an autoclave at 580 degrees C which is much lower than those of traditional methods. X-ray diffraction result indicates the formation of hexagonal A1N nanocrystallites. Transmission electron microscopy image shows that the average size of the crystallites is 6 nm. The possible synthetic mechanism of A1N is proposed.
引用
收藏
页码:1239 / 1240
页数:2
相关论文
共 16 条
[1]   Self-organized growth of nanostructure arrays on strain-relief patterns [J].
Brune, H ;
Giovannini, M ;
Bromann, K ;
Kern, K .
NATURE, 1998, 394 (6692) :451-453
[2]   Probing electrical transport in nanomaterials: Conductivity of individual carbon nanotubes [J].
Dai, HJ ;
Wong, EW ;
Lieber, CM .
SCIENCE, 1996, 272 (5261) :523-526
[3]  
Dean J.A., 1985, LANGES HDB CHEM, V13
[4]   Morphological control of nanocrystalline aluminum nitride: Aluminum chloride-assisted nanowhisker growth [J].
Haber, JA ;
Gibbons, PC ;
Buhro, WE .
JOURNAL OF THE AMERICAN CHEMICAL SOCIETY, 1997, 119 (23) :5455-5456
[5]  
HWANG CC, 1997, INT J SELF PROPAG HI, V6, P419
[6]   TRANSPARENT AIN CERAMICS [J].
KURAMOTO, N ;
TANIGUCHI, H .
JOURNAL OF MATERIALS SCIENCE LETTERS, 1984, 3 (06) :471-474
[7]  
Laitinen H.A., 1975, Chemical Analysis
[8]  
Marchant D. D., 1989, ADV CERAM, V26, P19
[9]   ALN POWDER SYNTHESIS VIA NITRIDING REACTION OF ALUMINUM SUB-CHLORIDE [J].
OHHASHI, T ;
NISHIDA, T ;
SUGIURA, M ;
FUWA, A .
MATERIALS TRANSACTIONS JIM, 1993, 34 (06) :541-547