Synthesis and characterization of MgAl2O4 spinel precursor from a heterogeneous alkoxide solution containing fine MgO powder

被引:88
作者
Shiono, T [1 ]
Shiono, K [1 ]
Miyamoto, K [1 ]
Pezzotti, G [1 ]
机构
[1] Kyoto Inst Technol, Dept Chem & Mat Technol, Kyoto 6068585, Japan
关键词
Alkoxide solution - Boehmite - Hydroxide - Magnesium aluminate;
D O I
10.1111/j.1151-2916.2000.tb01180.x
中图分类号
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
A precursor was synthesized from a heterogeneous alkoxide solution that contained fine MgO powder, which allowed the preparation of MgAl2O4 spinel powder with high sinterability characteristics. The precursor consisted of a mixture of boehmite (AlO(OH)) and a mixed hydroxide (Mg4Al2(OH)(14). 3H(2)O). The spinel phase formed through two steps: (i) decomposition of the mixed hydroxide at low temperature and (ii) solid-state reaction between MgO and gamma-Al2O3 at higher temperatures. Dense polycrystalline spinel could be obtained from the calcined powders at sintering temperatures as low as 1400 degrees C.
引用
收藏
页码:235 / 237
页数:3
相关论文
共 10 条
[1]  
BAKKER WT, 1967, AM CERAM SOC BULL, V46, P1094
[2]  
BRATTON RJ, 1969, AM CERAM SOC BULL, V48, P759
[3]  
HOKAZONO S, 1992, BRIT CERAM TRANS J, V91, P77
[4]  
KANZAKI S, 1983, YOGYO-KYOKAI-SHI, V91, P164
[5]  
Nakagawa Z., 1982, Yogyo-Kyokai-Shi, V90, P312, DOI 10.2109/jcersj1950.90.1042_312
[6]  
SHIONO T, 1991, CERAMIC T, V22, P69
[7]  
SHIONO T, 1994, J JPN SOC POWDER POW, V41, P573
[8]  
Sugiura M., 1984, Yogyo-Kyokai-Shi, V92, P605, DOI 10.2109/jcersj1950.92.1071_605
[9]   PREPARATION OF MGAL2O4 SPINEL POWDERS VIA FREEZE-DRYING OF ALKOXIDE PRECURSORS [J].
WANG, CT ;
LIN, LS ;
YANG, SJ .
JOURNAL OF THE AMERICAN CERAMIC SOCIETY, 1992, 75 (08) :2240-2243
[10]  
YAMAGUCHI O, 1975, J JPN SOC POWDER POW, V22, P202