Nano Fe2O3 embedded in montmorillonite with citric acid enhanced photocatalytic activity of nanoparticles towards diethyl phthalate

Nano-Fe2O3 embedded in montmorillonite particles (Fe-Mt) were prepared to degrade diethyl phthalate (DEP) with citric acid (CA) under xenon light irradiation. Compared to pristine montmorillonite (Na-Mt), the embedding process increased 14.5-fold of iron content and 1.8-fold of specific surface area. The synthesized Fe-Mt have more oxygen vacancies than Fe2O3 nanoparticles (nFe(2)O(3)), which could induce more reactive oxygen species (ROSs) generation in the presence of CA under xenon lamp irradiation. Fe-Mt with CA enhanced photo-assisted degradation of DEP 2.5 times as compared to nFe(2)O(3) with CA. Quenching experiments, electron paramagnetic resonance (EPR) spectroscopy and identification of products confirmed that surface-bound center dot OH was the main radical to degrade DEP. Common anions (i.e., NO3-, CO32-, Cl-) and humic acid could compete center dot OH with DEP and cause slower degradation of DEP. The removal efficiency of DEP was more than 56% with Fe-Mt after three recycles, and the dissolved Fe concentration from Fe-Mt was below 75 mu mol/L, indicating Fe-Mt had a good stability as a catalyst. Fe-Mt together with CA appeared to be a promising strategy to remove organic pollutants in surface water, or topsoil under solar irradiation. (C) 2020 The Research Center for Eco-Environmental Sciences, Chinese Academy of Sciences. Published by Elsevier B.V.