The solubility of C in solid Cu

被引：284
作者：
López, GA
Mittemeijer, E
机构：
[1] Univ Stuttgart, Max Planck Inst Met Res, D-70569 Stuttgart, Germany
[2] Univ Stuttgart, Inst Phys Met, D-70569 Stuttgart, Germany
来源：
SCRIPTA MATERIALIA | 2004年 / 51卷 / 01期
关键词：
solubility of C in solid Cu; Cu-C system; interstitial solid solutions; combustion analysis;
D O I：
10.1016/j.scriptamat.2004.03.028
中图分类号：
TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
The solubility of C in solid Cu was determined in the temperature range 1143-1293 K. Layers of C were vapour deposited onto high-purity Cu slices, which were annealed for 72 and 240 h at different temperatures. The C content in the samples was determined by means of combustion analysis. A Henrian behaviour for the carbon activity in the interstitial solid solution was observed. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.
引用
收藏
页码：1 / 5
页数：5
相关论文
共 11 条
[1]  
BEVER MB, 1946, T AM I MIN MET ENG, V166, P128
[2]   Diffusivity of carbon in the copper matrix. Influence of alloying [J].
Dorfman, S ;
Fuks, D .
COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 1996, 27 (09) :697-701
[3]   Stability of copper segregations on copper/carbon metal-matrix composite interfaces under alloying [J].
Dorfman, S ;
Fuks, D .
COMPOSITES SCIENCE AND TECHNOLOGY, 1997, 57 (08) :1065-1069
[4]   A MODIFIED COMBUSTION METHOD FOR THE DETERMINATION OF THE SURFACE AND BULK CARBON CONTENTS OF HIGH-PURITY METALS [J].
GRETZINGER, K ;
GRALLATH, E ;
TOLG, G .
ANALYTICA CHIMICA ACTA, 1987, 193 :1-18
[5]   IMPROVEMENTS IN THE COMBUSTION METHOD FOR THE DETERMINATION OF LOW-CARBON CONTENTS IN STEEL [J].
GRUNER, W ;
GRALLATH, E .
STEEL RESEARCH, 1995, 66 (11) :455-457
[6]  
LECLAIRE AD, 1990, DIFFUSION SOLID META, V26, P498
[7]   SOLUBILITY OF CARBON IN SILVER, COPPER AND GOLD [J].
MATHIEU, G ;
GUIOT, S ;
CABANE, J .
SCRIPTA METALLURGICA, 1973, 7 (04) :421-425
[8]   SOLUBILITY OF CARBON IN SOLID GOLD COPPER AND SILVER [J].
MCLELLAN, RB .
SCRIPTA METALLURGICA, 1969, 3 (06) :389-&
[9]  
MCLELLAN RB, 1966, PHASE STABILITY META, P398
[10]   CU-C AND AL-CU-C PHASE-DIAGRAMS AND THERMODYNAMIC PROPERTIES OF C IN THE ALLOYS FROM 1550-DEGREES-C TO 2300 DEGREES-C [J].
ODEN, LL ;
GOKCEN, NA .
METALLURGICAL TRANSACTIONS B-PROCESS METALLURGY, 1992, 23 (04) :453-458
12