Processing and Properties of Tungsten-Steel Composites and FGMs Prepared by Spark Plasma Sintering

Tungsten is the prime candidate material for the plasma-facing components of fusion reactors. For the joining of tungsten armor to the cooling system or support structure, composites or graded interlayers can be used to reduce the stress concentration at the interface. These interlayers can be produced by several technologies. Among these, spark plasma sintering appears advantageous because of its ability to fabricate fully dense parts at lower temperatures and in a shorter time than traditional powder metallurgy techniques, thanks to the concurrent application of temperature, pressure, and electrical current. In this work, spark plasma sintering of tungsten-steel composites and functionally graded layers (FGMs) was investigated. As a first step, pure tungsten and steel powders of different sizes were sintered at a range of temperatures to find a suitable temperature window for fully dense compacts. Characterization of the sintered compacts included structure (by SEM); porosity (by the Archimedean method and image analysis); thermal diffusivity (by the flash method) and mechanical properties (microhardness and flexural strength). Compacts with practically full density and fine grains were obtained; while the temperature needed to achieve full sintering decreased with decreasing powder size (down to about 1500 degrees C for the 0.4 mu m powder). For fully sintered compacts, the hardness and thermal diffusivity increased with decreasing powder size. Composites with selected tungsten/steel ratios were produced at several conditions and characterized. At temperatures of 1100 degrees C or above, intermetallic formation was observed in the composites; nevertheless, without a detrimental effect on the mechanical strength. Finally, the formation of graded layers and tungsten-steel joints in various configurations was demonstrated.