Properties of mechanically alloyed P/M composites of Al-Mg2Si-oxide systems

被引:8
|
作者
Sugamata, M. [1 ]
Shiina, K. [1 ]
Kubota, M. [1 ]
Kaneko, J. [1 ]
机构
[1] Nihon Univ, Coll Ind Technol, Chiba 2758575, Japan
关键词
Powder metallurgy; Mechanical alloying; Aluminum; Magnesium silicide; Oxide; Mechanical property; POWDERS;
D O I
10.1016/j.jallcom.2008.07.201
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
With a purpose of obtaining light-weight materials of high strength, mixture of aluminum powder and Mg2Si powder at the composition of Al-20mass%Mg2Si2 was mechanically alloyed with addition of oxide (Cr2O3, Fe2O3, MnO2) powders. Mechanical alloying was conducted by using an Attritor-type ball mill under argon atmosphere. The mechanically alloyed powders were consolidated to the P/M materials by vacuum hot pressing and hot extrusion. Solid-state reactions during mechanical alloying and subsequent thermomechanical processing were studied. Their structures and mechanical properties were examined and compared with hyper-eutectic Al-Si based P/M materials. All added oxides were decomposed and aluminide compounds were formed during heating of the extruded P/M materials. Mg2Si was only partially decomposed after heating P/M materials. All the P/M materials of Al-Mg2Si-oxide showed high compressive strength above 900 MPa. Among them, the highest strength of 1090 MPa was obtained for Al-Mg2Si-Fe2O3. Even the P/M material of Al-Mg2Si without oxide addition showed compressive strength of 795 MPa. The Al-Mg2Si based P/M materials showed higher compressive strength and higher ductility than hyper-eutectic AI-Si based P/M materials. Crown Copyright (C) 2008 Published by Elsevier B.V. All rights reserved.
引用
收藏
页码:350 / 354
页数:5
相关论文
共 50 条
  • [1] Mechanically alloyed P/M composites of Al-Mg-silicide and Al-Mg-oxide systems
    Kaneko, J.
    Sugamata, M.
    Akiyama, H.
    THERMEC 2006, PTS 1-5, 2007, 539-543 : 854 - +
  • [2] Microstructure and mechanical properties of mechanically alloyed intermetallic Mg2Si-Al alloys
    Frommeyer, Georg
    Beer, Stephan
    von Oldenburg, Kersten
    Zeitschrift fuer Metallkunde/Materials Research and Advanced Techniques, 1994, 85 (05): : 372 - 377
  • [3] MICROSTRUCTURE AND MECHANICAL-PROPERTIES OF MECHANICALLY ALLOYED INTERMETALLIC MG2SI-AL ALLOYS
    FROMMEYER, G
    BEER, S
    VONOLDENBURG, K
    ZEITSCHRIFT FUR METALLKUNDE, 1994, 85 (05): : 372 - 377
  • [4] MAGNETIC-PROPERTIES OF NANOCRYSTALLINE MECHANICALLY ALLOYED FE-M (M = AL, SI, CU)
    KUHRT, C
    SCHULTZ, L
    IEEE TRANSACTIONS ON MAGNETICS, 1993, 29 (06) : 2667 - 2669
  • [5] PREFERENTIAL OXIDATION OF MG IN MECHANICALLY ALLOYED AL-MG-O BASED SYSTEMS
    KIM, DG
    KANEKO, J
    SUGAMATA, M
    MATERIALS TRANSACTIONS JIM, 1995, 36 (02): : 305 - 311
  • [6] Consolidation and mechanical properties of mechanically alloyed Al-Mg powders
    Sakaliyska, Mira
    Scudino, Sergio
    Nguyen, Hoang Viet
    Surreddi, Kumar Babu
    Bartusch, Birgit
    Ali, Fahad
    Kim, Ji-Soon
    Eckert, Juergen
    ADVANCED INTERMETALLIC-BASED ALLOYS FOR EXTREME ENVIRONMENT AND ENERGY APPLICATIONS, 2009, 1128 : 299 - +
  • [7] Effect of additives on the hydrogen sorption properties of mechanically alloyed composites based on Mg and Mg2Ni
    Grigorova, E
    Khristov, A
    Khrussanova, M
    Bobet, JL
    Peshev, P
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2005, 30 (10) : 1099 - 1105
  • [8] Development of Heat-Resistant Composites Based on Al-Mg-Si Alloy Mechanically Alloyed with Aluminide Particles
    Prosviryakov, A. S.
    Bazlov, A. I.
    Mikhaylovskaya, A. V.
    JOM, 2024, 76 (03) : 1306 - 1318
  • [9] Development of Heat-Resistant Composites Based on Al-Mg-Si Alloy Mechanically Alloyed with Aluminide Particles
    A. S. Prosviryakov
    A. I. Bazlov
    A. V. Mikhaylovskaya
    JOM, 2024, 76 : 1306 - 1318
  • [10] STRUCTURES AND PROPERTIES OF MECHANICALLY ALLOYED ALUMINUM-METAL OXIDE POWDERS AND THEIR P/M MATERIALS
    KIM, DG
    KANEKO, J
    SUGAMATA, M
    JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1993, 57 (06) : 679 - 685