Structural evolutions of mechanically alloyed and heat treated Ti50C50 and Ti33B67 powders

被引：11

作者：

Tang, W. M. ^{[1
]}

Zheng, Z. X. ^{[1
]}

Wu, W. C. ^{[1
]}

Lu, J. ^{[1
]}

Liu, J. W. ^{[1
]}

Wang, J. M. ^{[1
]}

机构：

[1] Hefei Univ Technol, Sch Mat Sci & Engn, Hefei 230009, Peoples R China

来源：

MATERIALS CHEMISTRY AND PHYSICS | 2006年 / 99卷 / 01期

关键词：

TiC; TiB2; mechanical alloying; structural evolution; heat treatment; reaction mechanism;

D O I：

10.1016/j.matchemphys.2005.09.085

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

The TiC and TiB2 powders were successfully synthesized by ball milling the Ti50C50 and Ti33B67 elemental powders, respectively. During ball milling the Ti50C50 powder, a solid solution of C in Ti, Ti(C), was first formed, followed by TiC. After milling for 80 h, the powder was composed of TiC with grain size of 6 nm and a small amount of Ti(C) which was finally completely transformed to TiC after heat treatment. During ball milling the Ti33B67 powder, a solid solution of B in Ti, Ti(B), was first formed followed by the formation of an amorphous structure which transformed into a hexagonal phase of TiB2 with grain size of about 10 nm. (c) 2005 Elsevier B.V. All rights reserved.

引用

页码：144 / 149

页数：6

共 17 条

[11]

Murty BS, 1998, INT MATER REV, V43, P101, DOI 10.1179/095066098790105654

[12]

OARK YH, 1994, MAT SCI ENG A-STRUCT, V181, P1291

[13] Mechanical alloying and milling [J].

Suryanarayana, C .

PROGRESS IN MATERIALS SCIENCE, 2001, 46 (1-2) :1-184

[14] Self-sustaining reactions induced by ball milling [J].

Takacs, L .

PROGRESS IN MATERIALS SCIENCE, 2002, 47 (04) :355-414

[15] X-RAY LINE BROADENING FROM FILED ALUMINIUM AND WOLFRAM [J].

WILLIAMSON, GK ;

HALL, WH .

ACTA METALLURGICA, 1953, 1 (01) :22-31

[16]

YANG CF, 1995, J MATER SCI TECHNOL, V11, P217

[17] Different reaction mechanisms during mechanical alloying Ti50C50 and Ti33B67 [J].

Ye, LL ;

Liu, ZG ;

Quan, MX ;

Hu, ZQ .

JOURNAL OF APPLIED PHYSICS, 1996, 80 (03) :1910-1912

← 1 2 →