Effect of specimen size on ductile to brittle transition behavior of martensitic 9Cr steels after various heat treatments

被引:9
作者
Abe, F [1 ]
Kayano, H [1 ]
机构
[1] TOHOKU UNIV,INST MAT RES,OARAI BRANCH,OARAI,IBARAKI 31113,JAPAN
关键词
D O I
10.1016/0022-3115(96)00386-8
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The effect of specimen size on the ductile to brittle transition behavior has been investigated using the full-size and 1/3-size Charpy V-notch specimens of martensitic 9Cr-WVTa steels after quenching, tempering and subsequent prolonged aging treatments. The upper shelf energy (USE) and ductile to brittle transition temperature (DBTT) were widely changed by the heat treatments; the USE varied from 90 to 292 J, and the DBTT from 188 to 325 K. The nominal volume (Bb)(3/2), where B is the specimen thickness and b the ligament size, was effective as a normalization factor for the USE only in the large USE region above 210 and 8.5 J for the full-size and 1/3-size specimens, respectively. A new normalization factor depending on the USE level was proposed. Although the relationship between the DBTT for the full-size and 1/3-size specimens was different from steel to steel, the shift in DBTT caused by the heat treatments was described by Delta DBTT1/3-size = (1.2 +/- 0.1)Delta DBTTfull-size for all the steels examined.
引用
收藏
页码:44 / 51
页数:8
相关论文
共 16 条
[1]   EFFECT OF SPECIMEN SIZE ON THE DUCTILE BRITTLE TRANSITION BEHAVIOR AND THE FRACTURE SEQUENCE OF 9CR-W STEELS [J].
ABE, F ;
NODA, T ;
ARAKI, H ;
OKADA, M ;
NARUI, M ;
KAYANO, H .
JOURNAL OF NUCLEAR MATERIALS, 1987, 150 (03) :292-301
[2]  
ABE F, 1992, MATER SCI TECH SER, V8, P767, DOI 10.1179/026708392790171314
[3]   DEVELOPMENT OF REDUCED-ACTIVATION MARTENSITIC 9CR STEELS FOR FUSION-REACTOR [J].
ABE, F ;
NODA, T ;
ARAKI, H ;
OKADA, M .
JOURNAL OF NUCLEAR SCIENCE AND TECHNOLOGY, 1994, 31 (04) :279-292
[4]   OPTIMUM ALLOY COMPOSITIONS IN REDUCED-ACTIVATION MARTENSITIC 9CR STEELS FOR FUSION-REACTOR [J].
ABE, F ;
NODA, T ;
OKADA, M .
JOURNAL OF NUCLEAR MATERIALS, 1992, 195 (1-2) :51-67
[5]  
*ASTM, 1977, E23 ASTM 10, P230
[6]  
CORWIN WR, 1984, J NUCL MATER, V122, P342
[7]  
CORWIN WR, 1986, ASTM STP, V888, P325
[8]  
HU WL, 1983, P C FERRITIC ALLOYS, P631
[9]  
HU WL, 1983, HEDLSA2947FP
[10]  
KAYANO H, 1984, J NUCL MATER, V122, P649