The effect of variation of microstructure on fracture mechanics parameters of HSLA-100 steel

被引:42
作者
Das, S. K.
Sivaprasad, S.
Das, S.
Chatterjee, S. [1 ]
Tarafder, S.
机构
[1] Bengal Engn & Sci Univ, Sibpur, Howrah, India
[2] Natl Met Lab, Jamshedpur 831007, Bihar, India
来源
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING | 2006年 / 431卷 / 1-2期
关键词
ageing; Cu-precipitation; HSLA steel; microstructure; fracture toughness; FCGR curve;
D O I
10.1016/j.msea.2006.05.093
中图分类号
TB3 [工程材料学];
学科分类号
0805 ; 080502 ;
摘要
The variations in the FCGR curve, the J-R curve, the blunting-line slope and the stretch zone width (SZW) for systematic variation of microstructure in Cu-strengthened HSLA-100 steel has been studied. The microstructural variation in the steel has been introduced through ageing at various temperatures after an initial quenching treatment. This has resulted in progressive tempering of the as-quenched martensitic matrix, accompanied by nanoscale precipitation of coherent Cu particles that gradually coarsen and loose coherency with overageing. It was observed that although there was a systematic trend, the FCGR curves were least sensitive to microstructural changes. The variation of fracture toughness, characterized by J(Q) in most cases and by K-Q for the microstructures displaying highest strengths, correlated well with the inverse relationship between fracture toughness and strength. A systematic trend was also observed for the pre-exponent and exponent of the power-law tearing curve (for cases in which brittle fracture was precluded), the blunting-line slope and the SZW. The effect of coherency of precipitates in restricting plastic flow, as implied from the variation of mechanical properties with ageing temperature is thought to be responsible for the effects observed. (c) 2006 Published by Elsevier B.V.
引用
收藏
页码:68 / 79
页数:12
相关论文
共 20 条
[1]  
[Anonymous], 2003, ANN BOOK ASTM STAND, V04.05
[2]  
[Anonymous], 1999, D460794 ASTM
[3]  
CHRISTEIN JP, 1995, J SHIP PROD, V11, P97
[4]  
Czyryca E.J., 1993, Key Engineering Materials, V84, P491, DOI 10.4028/www.scientific.net/kem.84-85.491
[5]   DEVELOPMENT AND CERTIFICATION OF HSLA-100 STEEL FOR NAVAL SHIP CONSTRUCTION [J].
CZYRYCA, EJ ;
LINK, RE ;
WONG, RJ ;
AYLOR, DA ;
MONTEMARANO, TW ;
GUDAS, JP .
NAVAL ENGINEERS JOURNAL, 1990, 102 (03) :63-82
[6]  
DAS SK, IN PRESS MAT SCI TEC
[7]   Isothermal transformation products in a Cu-bearing high strength low alloy steel [J].
Dunne, DP ;
Ghasemi, SS ;
Yu, D .
ISIJ INTERNATIONAL, 1996, 36 (03) :324-333
[8]   MEASUREMENTS OF STRETCHED ZONE WIDTH (SZW) - A ROUND ROBIN PROGRAM OF EUROPEAN GROUP ON FRACTURE [J].
HALIM, A ;
DAHL, W ;
HAGEDORN, KE .
ENGINEERING FRACTURE MECHANICS, 1988, 31 (05) :857-866
[9]  
KOBAYASHI H, 1983, ASTM STP, V803, P438
[10]   MICROSTRUCTURE OF A QUENCHED AND TEMPERED CU-BEARING HIGH-STRENGTH LOW-ALLOY STEEL [J].
MIGLIN, MT ;
HIRTH, JP ;
ROSENFIELD, AR ;
CLARK, WAT .
METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1986, 17 (05) :791-798