Microstructure change caused by (Cr,Fe)23C6 carbides in high chromium Fe-Cr-C hardfacing alloys

被引：125

作者：

Fan, Chieh ^{[1
]}

Chen, Ming-Che ^{[1
]}

Chang, Chia-Ming ^{[1
]}

Wu, Weite ^{[1
]}

机构：

[1] Natl Chung Hsing Univ, Dept Mat Engn, Taichung 40227, Taiwan

来源：

SURFACE & COATINGS TECHNOLOGY | 2006年 / 201卷 / 3-4期

关键词：

hardness; hardfacing; welding; chromium carbide; chromium alloy;

D O I：

10.1016/j.surfcoat.2006.01.010

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

A series of high chromium Fe-Cr-C hardfacing alloys were produced by gas tungsten arc welding (GTAW). Chromium and graphite alloy fillers were used to deposit coatings on ASTM A36 steel substrates. These coatings were especially designed to vary the size and proportion of the (Cr,Fe)(23)C-6 carbides that are present in the microstructure at room temperature. Depending on the three different graphite additions of those alloy fillers, hypoeutectic, eutectic and hypereutectic microstructures were obtained on coated surfaces. No crack formation was found on the coatings. According to the X-ray diffraction analysis and microstructure characteristics, the hypercutectic composites consist of three phases, i.e. Cr-Fe solid solution (a), (CrFe)(23)C-6 and trace amounts of (Cr,Fe)(7)C-3. Massive (CrFe)(23)C-6 contain (CrFe)(7)C-3 in the center, and cause its high hardness value up to HRC 70. And the massive (Cr,Fe)(23)C-6 are surrounded by a eutectic structure to restrain cracks from appearing. All the microstructure constituents were rationalized in terms of a ternary diagram. (c) 2006 Elsevier B.V. All rights reserved.

引用

页码：908 / 912

页数：5

共 15 条

[1] Sliding wear of graphite crystallized chromium white cast iron [J].

Aso, S ;

Goto, S ;

Komatsu, Y ;

Hartono, W .

WEAR, 2001, 250 :511-517

[2] Comparison of wear resistant MMC and white cast iron [J].

Berns, H .

WEAR, 2003, 254 (1-2) :47-54

[3]

Bungardt K., 1958, ARCH EISENHUTTENWES, V29, P193

[4] Tungsten-inert gas surface alloying of a low carbon steel [J].

Eroglu, M ;

Ozdemir, N .

SURFACE & COATINGS TECHNOLOGY, 2002, 154 (2-3) :209-217

[5]

GRIFFING NR, 1962, T METALL SOC AIME, V224, P148

[6] Microstructure and wear characteristics of cobalt-based alloy deposited by plasma transferred arc weld surfacing [J].

Hou, QY ;

Gao, JS ;

Zhou, F .

SURFACE & COATINGS TECHNOLOGY, 2005, 194 (2-3) :238-243

[7]

JACKSON RS, 1970, J IRON STEEL I, V208, P163

[8] Microstructural characterization of high-carbon ferrochromium [J].

Lesko, A ;

Navara, E .

MATERIALS CHARACTERIZATION, 1996, 36 (4-5) :349-356

[9] Microstructure and mechanical properties of Fe-Cr-C eutectic composites [J].

Lu, LM ;

Soda, H ;

McLean, A .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 347 (1-2) :214-222

[10] Solidification and abrasion wear of white cast irons alloyed with 20% carbide forming elements [J].

Matsubara, Y ;

Sasaguri, N ;

Shimizu, K ;

Yu, S ;

Yu, K .

WEAR, 2001, 250 (250-251) :502-510

← 1 2 →