Investigation on mechanical properties and microstructure of silicon nitride ceramics fabricated by spark plasma sintering

In order to prepare high-performance and stable performance silicon nitride-based ceramic cutting tools, or- thogonal experiment was carried out firstly to study the influence of sintering temperature and sintering aids (MgSiN2, Y2O3 and CeO2) on the densification and mechanical properties of the Si3N4 materials by spark plasma sintering. The results showed that Si3N4 ceramics with 5 wt%MgSiN2, 3 wt%Y2O3 and 1 wt%CeO2 sintering aids had the best relative density and mechanical properties at 1650 degrees C. Secondly, the effects of sintering temperature on the densification, microstructure and mechanical properties of Si3N4 ceramics with 5 wt%MgSiN2, 3 wt%Y2O3 and 1 wt%CeO2 sintering aids were studied in detail. The results showed that the relative density of Si3N4 ceramics reached the maximum of 99.40 +/- 0.14% at 1650 degrees C, the Vickers hardness and fracture toughness were 16.53 +/- 0.12 GPa and 6.89 +/- 0.20 MPam(1/2 ), respectively. The grain shapes were composed of equiaxed alpha- Si3N4 and long columnar beta- Si3N4, and the transformation rate of alpha- Si3N4 to beta- Si(3)N(4 )was 42.5%. Finally, the statistical distribution of the relative density, phase transformation rate and mechanical properties of Si3N4 ceramics with 5 wt%MgSiN2, 3 wt%Y2O3 and 1 wt%CeO2 sintering aids at 1650 degrees C was investigated. It was found that the mechanical properties of silicon nitride ceramics sintered by spark plasma sintering were less dispersive, and the hardness and fracture toughness obeyed the two parameters Weibull distribution well.