Pitting of AISI 304L stainless steel coated with nano structured sol-gel alumina coatings in chloride containing acidic environments

被引：33

作者：

Ruhi, G. ^{[1
]}

Modi, O. P. ^{[1
]}

Singh, I. B. ^{[1
]}

机构：

[1] CSIR, Adv Mat & Proc Res Inst, Bhopal 462064, Madhya Pradesh, India

来源：

CORROSION SCIENCE | 2009年 / 51卷 / 12期

关键词：

Steel; SEM; AFM; EIS; Pitting corrosion; CORROSION-RESISTANCE; FILMS; TEMPERATURE; 304-STAINLESS-STEEL; PARAMETER; BEHAVIOR; ALLOYS; WEAR;

D O I：

10.1016/j.corsci.2009.08.037

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Sol-gel coatings were applied on AISI 304L stainless steel and their pitting resistance was evaluated in different concentrations of chloride ions in 0.01 M H2SO4 solution. AFM and XRD analyses of the coated surface confirmed the presence of nano structured alpha-alumina phase in the coating. Anodic polarisation indicated a considerable shift of pitting potential of the substrate in the noble direction after applying coatings. The SEM micrographs of the polarised specimens revealed the presence of relatively less number of pits on the coated surface. EIS analysis demonstrated the occurrence of diffusion process at the coating/metal interfaces in chloride ions presence. (C) 2009 Elsevier Ltd. All rights reserved.

引用

页码：3057 / 3063

页数：7

共 45 条

[41] The characterization and corrosion resistance of cerium chemical conversion coatings for 304 stainless steel [J].

Wang, C ;

Jiang, F ;

Wang, FH .

CORROSION SCIENCE, 2004, 46 (01) :75-89

[42] Corrosion characteristics of coloured films on stainless steel formed by chemical, INCO and ac processes [J].

Wang, JH ;

Duh, JG ;

Shih, HC .

SURFACE & COATINGS TECHNOLOGY, 1996, 78 (1-3) :248-254

[43] EFFECTS OF CL- CONCENTRATION AND TEMPERATURE ON PITTING OF ALSL-304 STAINLESS-STEEL [J].

WANG, JH ;

SU, CC ;

SZKLARSKASMIALOWSKA, Z .

CORROSION, 1988, 44 (10) :732-737

[44] Influence of ultrasound on pitting corrosion and crevice corrosion of SUS304 stainless steel in chloride sodium aqueous solution [J].

Wang, Rongguang .

CORROSION SCIENCE, 2008, 50 (02) :325-328

[45] Corrosion behavior of 304 stainless steel in high temperature, hydrogenated water [J].

Ziemniak, SE ;

Hanson, M .

CORROSION SCIENCE, 2002, 44 (10) :2209-2230

← 1 2 3 4 5 →