Research on the process of micro-crack damage evolution and coalescence in brittle materials

Damage and failure of quasi-brittle materials are caused by evolution and coalescence of micro-cracks. To solve the problem of elliptical micro-crack growth at the elastic deformation stage, a method of complex potential functions is proposed and the effect of the initial orientation on micro-crack growth and deflection is discussed. The critical stress condition for the initial damage is derived according to the criterion of micro-crack growth. Based on energy conservation during wing-crack propagation, a damage constitutive model is developed with the strain criterion created in the condition of micro-crack coalescence. The stress-strain curves of quasi-brittle materials in uniaxial compression obtained based on this model are examined with the experimental results. In conclusion, (1) wing crack growth, propagation, and coalescence at the tips of micro-cracks eventually lead to the formation of an anisotropic effective compliance tensor in the damaged material; (2) a large number of micro-crack coalescence is a highly nonlinear phenomenon resulting in failure of materials; and (3) the effective elastic modulus of damaged material decreases with the wing crack propagation length increasing. (C) 2013 Elsevier Ltd. All rights reserved.