MICROSTRUCTURE AND PROPERTIES OF IN SITU SYNTHESIZED ZrC-ZrB2/Fe COMPOSITE COATING PRODUCED BY GTAW

被引：5
作者：
Wang, Zhenting [1 ,2 ]
Chen, Lili [2 ]
Zhang, Xianyou [1 ]
机构：
[1] Harbin Univ Sci & Technol, Mobile Postdoctoral Ctr Mat Sci & Engn, Harbin, Peoples R China
[2] Heilongjiang Inst Sci & Technol, Coll Mat Sci & Engn, Harbin, Heilongjiang, Peoples R China
来源：
INTERNATIONAL JOURNAL OF MODERN PHYSICS B | 2009年 / 23卷 / 6-7期
关键词：
Composite coating; GTAW; microstructure; microhardness; wear resistance; SURFACE; ZRC;
D O I：
10.1142/S0217979209061068
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
A metal matrix composite coating reinforced by ZrC-ZrB2 particulates has been successfully fabricated utilizing the in situ reaction of Zr, B4C and Fe pre-placed mixed powders by gas tungsten arc welding (GTAW) cladding process. Various volume fraction of ZrC-ZrB2 particulates composite coatings were produced through cladding different weight ratios of Zr+B4C (30%, 50%, 70%) to improve the wear resistance of AISI1020 steel substrate. The Microstructure of the coating was analyzed by scanning electron microscopy (SEM), X-ray diffraction (XRD), energy-dispersive spectrum (EDS), meantime microhardness and wear resistance at room temperature of the composite coating were examined by means of Microhardness Tester and Wear Tester, respectively. The results show that the main phases of the composite coating obtained by GTAW are ZrC, ZrB2 and alpha-Fe, ZrC exhibits hexahedron and petal shapes, ZrC-ZrB2 compound presents acicular and clubbed forms. With the increase of content of Zr+B4C, the maximum volume fraction of ZrC-ZrB2 particulates can reach 16.5%, microhardness is up to 1300HV, and wear resistance is about twenty times higher than that of AISI1020 steel substrate.
引用
收藏
页码：1438 / 1443
页数：6
相关论文
共 12 条
  • [1] In situ synthesis of SiC reinforced MMC surface on AISI 304 stainless steel by TIG surface alloying
    Buytoz, S
    Ulutan, M
    [J]. SURFACE & COATINGS TECHNOLOGY, 2006, 200 (12-13) : 3698 - 3704
  • [2] DU BS, 2007, T CHINA WELDING I, V65, P28
  • [3] EROLU M, 2002, SURF COAT TECH, V209, P154
  • [4] Intermetallic coatings produced by TIG surface melting
    Mridha, S
    Ong, HS
    Poh, LS
    Cheang, P
    [J]. JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2001, 113 (1-3) : 516 - 520
  • [5] Mechanical activation assisted self-propagating high- temperature synthesis of ZrC and ZrB2 in air from Zr/B/C powder mixtures
    Tsuchida, T
    Yamamoto, S
    [J]. JOURNAL OF THE EUROPEAN CERAMIC SOCIETY, 2004, 24 (01) : 45 - 51
  • [6] TSUCHIDA T, 2004, SOLID STATE IONICS, V215, P177
  • [7] Reactive infiltration synthesis of TiB2-TiC particulates reinforced steel matrix composites
    Wang, HY
    Jiang, QC
    Ma, BX
    Wang, Y
    Zhao, F
    [J]. JOURNAL OF ALLOYS AND COMPOUNDS, 2005, 391 (1-2) : 55 - 59
  • [8] Fabricating TiC particles reinforced Fe-based composite coatings produced by GTAW multi-layers melting process
    Wang, X. H.
    Song, S. L.
    Zou, Z. D.
    Qu, S. Y.
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2006, 441 (1-2): : 60 - 67
  • [9] YOUNG K, 2003, MATER CHARACT, V31, P50
  • [10] Microstructure characteristics of ZrC-reinforced composite coating produced by laser cladding
    Zhang, QM
    He, JJ
    Liu, WJ
    Zhong, ML
    [J]. SURFACE & COATINGS TECHNOLOGY, 2003, 162 (2-3) : 140 - 146
12