Phase transformation and decomposition mechanisms of the β0(ω) phase in cast high Nb containing TiAl alloy

被引:65
作者
Song, L. [1 ]
Xu, X. J. [2 ]
You, L. [1 ]
Liang, Y. F. [1 ]
Lin, J. P. [1 ]
机构
[1] Univ Sci & Technol Beijing, State Key Lab Adv Met & Mat, Beijing 100083, Peoples R China
[2] Zhongyuan Univ Technol, Mat & Chem Sch, Zhengzhou 450007, Peoples R China
基金
中国国家自然科学基金;
关键词
Metals and alloys; TEM; Microstructure; Phase transformation; GAMMA-TITANIUM ALUMINIDES; ORDERED OMEGA-PHASES; THERMAL-STABILITY; BETA-PHASE; Y) ALLOY; MICROSTRUCTURE; EVOLUTION; BEHAVIOR;
D O I
10.1016/j.jallcom.2014.07.130
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
High Nb containing TiAl (Nb-TiAl) alloys are thought to be used at higher temperatures than the conventional TiAl alloys, typically up to 900 degrees C. However, the beta(0) and omega-related phases are usually induced by Nb-segregation in cast alloys. It is important to reveal the transformation mechanisms of the beta(0) and omega-related phases at elevated temperatures for better design of the alloy and optimizing the heat treatment process. In this study, the interconversion mechanism between the ordered omega and beta(0) phases and the decomposition process of the beta(0) phase in the as-cast Ti-45Al-8.5Nb-0.2W-0.2B-0.02Y (at.%) alloy are studied. The omega(0) particles grow up by richening Nb and rejecting W to the surrounding beta(0) matrix. The beta(0) and omega(0) phase are separated after annealing at 900 degrees C, whereas the omega(0) phase dissolves into the beta(0) matrix after annealing at 950 degrees C. The beta(0) and omega(0) phases undergo beta(0) -> gamma and omega(0) (B8(2) structure) -> D8(8)-omega (D8(8) structure) -> gamma transformation respectively during annealing, and the beta(0) -> gamma transformation can be achieved in several ways. The omega(0) particles with a high Nb content act as pinning points at the beta(0)/gamma boundaries during the beta(0) -> gamma transformation. The corresponding mechanisms of the transformations mentioned above are discussed. (C) 2014 Elsevier B.V. All rights reserved.
引用
收藏
页码:483 / 491
页数:9
相关论文
共 42 条
[1]   Coupling of displacive and replacive ordering [J].
Banerjee, S ;
Tewari, R ;
Mukhopadhyay, P .
PROGRESS IN MATERIALS SCIENCE, 1997, 42 (1-4) :109-123
[2]   THE FORMATION OF ORDERED OMEGA-RELATED PHASES IN ALLOYS OF COMPOSITION TI4AL3NB [J].
BENDERSKY, LA ;
BOETTINGER, WJ ;
BURTON, BP ;
BIANCANIELLO, FS ;
SHOEMAKER, CB .
ACTA METALLURGICA ET MATERIALIA, 1990, 38 (06) :931-943
[3]   ORDERED OMEGA-DERIVATIVES IN A TI-37.5AL-20NB AT-PERCENT ALLOY [J].
BENDERSKY, LA ;
BURTON, BP ;
BOETTINGER, WJ ;
BIANCANIELLO, FS .
SCRIPTA METALLURGICA ET MATERIALIA, 1990, 24 (08) :1541-1546
[4]   Micro segregation in high Nb containing TiAl alloy ingots beyond laboratory scale [J].
Chen, G. L. ;
Xu, X. J. ;
Teng, Z. K. ;
Wang, Y. L. ;
Lin, J. P. .
INTERMETALLICS, 2007, 15 (5-6) :625-631
[5]  
CHEN GL, 1993, STRUCTURAL INTERMETALLICS, P319
[6]  
Chen GL, 1999, GAMMA TITANIUM ALUMINIDES 1999, P371
[7]   Microstructure and fracture toughness of a β phase containing TiAl alloy [J].
Chen, Yuyong ;
Niu, Hongzhi ;
Kong, Fantao ;
Xiao, Shulong .
INTERMETALLICS, 2011, 19 (10) :1405-1410
[8]   The decomposition of the beta phase in Ti-44Al-8Nb and Ti-44Al-4Nb-4Zr-0.2Si alloys [J].
Cheng, TT ;
Loretto, MH .
ACTA MATERIALIA, 1998, 46 (13) :4801-4819
[9]  
Chladil HF, 2007, INT J MATER RES, V98, P1131, DOI 10.3139/146.101569
[10]   Design of novel β-solidifying TiAl alloys with adjustable β/B2-phase fraction and excellent hot-workability [J].
Clemens, Helmut ;
Wallgram, Wilfried ;
Kremmer, Sascha ;
Guether, Volker ;
Otto, Andreas ;
Bartels, Arno .
ADVANCED ENGINEERING MATERIALS, 2008, 10 (08) :707-713