Evaluation of strain hardening parameters

The plane-strain compression test for three kinds of materials was carried out in a temperature range between room temperature and 400 degreesC. The sigma-epsilon curves and strain-hardening rate at different temperatures were simulated and a reasonable fit to the experimental data was obtained. A modified model created by data inference and computer simulation was developed to describe the strain hardening at a large deformation, and the predicted strain hardening are in a good agreement with that observed in a large range of stress. The influences of different parameters on strain hardening behaviour under large deformation were analysed. The temperature increase within the test temperatures for stainless steel 18/8 Ti results in dropping of flow stress and strain-hardening rate. For favourable gamma-fibre texture to obtain high r, the cold rolling was applied at large reduction. In the experimental procedure, the X-ray diffraction test was carried out to compare the strain hardening and microstructure under large deformation for a bcc steel (low carbon steel SS-1142). The results indicate that the high strain-hardening rate possibly occurs when the primary slip plane 110 is parallel to the rolling plane and the strain-hardening rate decreases when lots of 110 plane rotate out from the orientation {110}//RP.