Translucency of glass-fibre-reinforced composite materials

被引:5
作者
Nakamura, T [1 ]
Tanaka, H [1 ]
Kawamura, Y [1 ]
Wakabayashi, K [1 ]
机构
[1] Osaka Univ, Grad Sch Dent, Course Integrated Oral Sci & Stomatol, Div Oromaxillofacial Regenerat, Suita, Osaka 5650871, Japan
关键词
glass-fibre; composite; colour; translucency; contrast ratio;
D O I
10.1111/j.1365-2842.2004.01296.x
中图分类号
R78 [口腔科学];
学科分类号
1003 ;
摘要
The purpose of this study was to examine the translucency of glass-fibre-reinforced composite framework materials. Vectris and FibreKor, as well as an experimental material, were the glass-fibre-reinforced framework materials used. Targis, Sculpture and Estenia were the types of particulate filler composites veneered onto frameworks. Specimens were fabricated from each material, 0.5 and 1.0 mm thick. In addition, laminate specimens, 1.5 mm thick, were fabricated. The translucency of each specimen was evaluated by determining its contrast ratio. The laminate specimens were examined for colour differences. The experimental framework material was more translucent than the enamel composite when it was not coloured, and was nearly as translucent as the dentine composite when coloured. The commercial tooth-coloured framework materials were nearly as translucent as the dentine composite. It was found that it was possible to reproduce the same colour as the veneering dentine composite, when the framework thickness was 0.5 mm, except in the case of FibreKor. Within the limitations of this study, tooth-coloured, glass-fibre-reinforced framework materials are nearly as translucent as the veneering dentine composite, but these materials affect the colour of the prosthesis if the thickness of the framework material is increased beyond a certain point.
引用
收藏
页码:817 / 821
页数:5
相关论文
共 20 条
  • [1] Antonson SA, 2001, INT J PROSTHODONT, V14, P316
  • [2] INFLUENCE OF P2O5, AGNO3, AND FECL3 ON COLOR AND TRANSLUCENCY OF LITHIA-BASED GLASS-CERAMICS
    ANUSAVICE, KJ
    ZHANG, NZ
    MOORHEAD, JE
    [J]. DENTAL MATERIALS, 1994, 10 (04) : 230 - 235
  • [3] Recycling of PET
    Awaja, F
    Pavel, D
    [J]. EUROPEAN POLYMER JOURNAL, 2005, 41 (07) : 1453 - 1477
  • [4] Flexural properties of fiber reinforced composite using a vacuum/pressure or a manual adaptation manufacturing process
    Behr, M
    Rosentritt, M
    Lang, R
    Handel, G
    [J]. JOURNAL OF DENTISTRY, 2000, 28 (07) : 509 - 514
  • [5] Freiberg RS, 1998, AM J DENT, V11, P214
  • [6] THE USE OF CONTINUOUS FIBER REINFORCEMENT IN DENTISTRY
    GOLDBERG, AJ
    BURSTONE, CJ
    [J]. DENTAL MATERIALS, 1992, 8 (03) : 197 - 202
  • [7] Grin D, 2000, J Dent Technol, V17, P16
  • [8] Höland W, 2000, J BIOMED MATER RES, V53, P297, DOI 10.1002/1097-4636(2000)53:4<297::AID-JBM3>3.0.CO
  • [9] 2-G
  • [10] Judd DB., 1975, Color in business, science, and industry /