Evaluation of hot corrosion behavior of CSZ, CSZ/micro Al2O3 and CSZ/nano Al2O3 plasma sprayed thermal barrier coatings

被引：66
作者：
Nejati, M. [1 ]
Rahimipour, M. R. [1 ]
Mobasherpour, I. [1 ]
机构：
[1] Mat & Energy Res Ctr, Dept Ceram, Karaj, Iran
来源：
CERAMICS INTERNATIONAL | 2014年 / 40卷 / 03期
关键词：
Thermal barrier coating; Hot corrosion; Plasma spray; CSZ/Al2O3; composite; ZIRCONIA COATINGS; MECHANICAL-PROPERTIES; STAINLESS-STEEL; BOND COAT; YTTRIA; ALUMINA; MICROSTRUCTURE; RESISTANCE; CERIA; DEGRADATION;
D O I：
10.1016/j.ceramint.2013.08.135
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Hot corrosion is one of the main destructive factors in thermal barrier coatings (TBCs) which come as a result of molten salt effect on the coating gas interface. Hot corrosion behavior of three types of plasma sprayed TBCs was evaluated: usual CSZ, layer composite of CSZ/Micro Al2O3 and layer composite of CSZ/Nano Al2O3 in which Al2O3 was as a topcoat on CSZ layer. Hot corrosion studies of plasma sprayed thermal barrier coatings (TBCs) were conducted in 45 wt% Na2SO4+55 wt% V2O5 molten salt at 1050 degrees C for 40 h. The graded microstructure of the coatings was examined using scanning electron microscope (SEM) and X-ray diffractometer (XRD) before and after hot corrosion test The results showed that no damage and hot corrosion products was found on the surface of CSZ/Nano Al2O3 coating and monoclinic ZrO2 fraction was lower in CSZ/Micro Al2O3 coating in comparison with usual CSZ. reaction of molten salts with stabilizers of zirconia (Y2O3 and CeO2) that accompanied by formation of monoclinic zirconia, irregular shape crystals of YVO4, CeVO4 and semi-cubic crystals of CeO2 as hot corrosion products, caused the degradation of CSZ coating in usual CSZ and CSZ/Micro Al2O3 coating. (C) 2013 Elsevier Ltd and Techna Group S.r.l. All rights reserved.
引用
收藏
页码：4579 / 4590
页数：12
相关论文
共 50 条
  • [1] Afrasiabi A., 2008, T JWRI, V37, P57
  • [2] A comparative study on hot corrosion resistance of three types of thermal barrier coatings:: YSZ, YSZ + Al2O3 and YSZ/Al2O3
    Afrasiabi, Abbas
    Saremi, Mohsen
    Kobayashi, Akira
    [J]. MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 478 (1-2): : 264 - 269
  • [3] Hot corrosion control in plasma sprayed YSZ coating by alumina layer with evaluation of microstrcuture and nanoindentation data (H, E)
    Afrasiabi, Abbas
    Kobayashi, Akira
    [J]. VACUUM, 2013, 88 : 103 - 107
  • [4] Evaluation of hot corrosion behavior of plasma sprayed ceria and yttria stabilized zirconia thermal barrier coatings in the presence of Na2SO4+V2O5 molten salt
    Ahmadi-Pidani, Raheleh
    Shoja-Razavi, Reza
    Mozafarinia, Reza
    Jamali, Hossein
    [J]. CERAMICS INTERNATIONAL, 2012, 38 (08) : 6613 - 6620
  • [5] Processing, Microstructure and Mechanical Properties of Air Plasma-Sprayed Ceria-Yttria Co-stabilized Zirconia Coatings
    Alfano, M.
    Di Girolamo, G.
    Pagnotta, L.
    Sun, D.
    [J]. STRAIN, 2010, 46 (05) : 409 - 418
  • [6] [Anonymous], P 1 INT THERM SPRAY
  • [7] Effect of critical plasma spray parameters on the microstructure, microhardness and wear and corrosion resistance of plasma sprayed alumina coatings
    Aruna, S. T.
    Balaji, N.
    Shedthi, Jyothi
    Grips, V. K. William
    [J]. SURFACE & COATINGS TECHNOLOGY, 2012, 208 : 92 - 100
  • [8] High performance nanostructured ZrO2 based thermal barrier coatings deposited by high efficiency supersonic plasma spraying
    Bai, Y.
    Han, Z. H.
    Li, H. Q.
    Xu, C.
    Xu, Y. L.
    Wang, Z.
    Ding, C. H.
    Yang, J. F.
    [J]. APPLIED SURFACE SCIENCE, 2011, 257 (16) : 7210 - 7216
  • [9] Evaluation of laser-glazed plasma-sprayed thermal barrier coatings under high temperature exposure to molten salts
    Batista, C.
    Portinha, A.
    Ribeiro, R. M.
    Teixeira, V.
    Oliveira, C. R.
    [J]. SURFACE & COATINGS TECHNOLOGY, 2006, 200 (24) : 6783 - 6791
  • [10] Chawla V., 2008, Mat. Forum, V32, P137
12345