Microanalysis of 9-12% chromium steels P92 and P122

被引:0
作者
Hättestrand, M [1 ]
Schwind, M [1 ]
Andrén, HO [1 ]
机构
[1] Chalmers Univ Technol, Dept Phys, SE-41296 Gothenburg, Sweden
来源
ADVANCED HEAT RESISTANT STEELS FOR POWER GENERATION | 1999年
关键词
D O I
暂无
中图分类号
TE [石油、天然气工业]; TK [能源与动力工程];
学科分类号
0807 ; 0820 ;
摘要
The 9-12% chromium steels P122 and P92 have been investigated using atom probe field ion microscopy (APFIM) and transmission electron microscopy (TEM). The two steels are similar in composition with the exception of an addition of copper to P122, allowing a higher chromium content. The investigated materials were tempered at 770 degrees C and isothermally aged at 600 degrees C for times ranging from 0 to 10 000 h. The matrix and precipitates of type M23C6, MX and Laves phase have been analysed with APFIM. Steel P122 contains 0.9% copper and it was found that the matrix concentration of copper drops during ageing from 0.4% to an equilibrium level at about 0.1%. No copper was found in M23C6, MX or Laves phase. Instead copper forms a separate phase, that was identified by TEM. During ageing the amount of tungsten in the matrix drops due to formation of Laves phase. This process is faster in steel P122 compared to steel P92, indicating an accelerating effect of copper on the nucleation of Laves phase. In both steels, enhanced concentrations of boron were found inside M23C6 carbides. Phosphorous was found to segregate to a very narrow region at the carbide/matrix interface. The role of different alloying elements in the two steels is discussed.
引用
收藏
页码:199 / 211
页数:13
相关论文
共 50 条
[41]   CROSS-WELD CREEP COMPARISON OF POWER PLANT STEELS CrMoV, P91 AND P92 [J].
Tanner, David W. J. ;
Sun, Wei ;
Hyde, Thomas H. .
PROCEEDINGS OF THE ASME PRESSURE VESSELS AND PIPING CONFERENCE, PVP 2012, VOL 6, PTS A AND B, 2012, :369-374
[42]   Hot workability behaviour of two P92 creep resistant steels: Constitutive analysis [J].
Obiko, Japheth ;
Whitefield, David ;
Bodunrin, Micheal .
INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2023, 129 (3-4) :1503-1512
[43]   Hot workability behaviour of two P92 creep resistant steels: Constitutive analysis [J].
Japheth Obiko ;
David Whitefield ;
Micheal Bodunrin .
The International Journal of Advanced Manufacturing Technology, 2023, 129 :1503-1512
[44]   COMPARISON OF RESULTS CORRELATIONS OF THE STEELS P91, P92 AND 15 313 AFTER CREEP SP TEST [J].
Volak, Josef ;
Bunda, Zbynek ;
Chvostova, Eva .
METAL 2013: 22ND INTERNATIONAL CONFERENCE ON METALLURGY AND MATERIALS, 2013, :856-860
[45]   Long-term thermal degradation of narrow gap orbital welded P91 and P92 steels [J].
Junek, Michal ;
Svobodova, Marie ;
Janovec, Jiri ;
Horvath, Jakub ;
Duchacek, Petr .
INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2020, 185
[46]   Alloy compositions and mechanical properties of 9-12% chromium steels with martensitic-austenitic microstructure [J].
Institute of Metallurgy, Swiss Fed. Inst. Technol., ETH-Z., Zürich, Switzerland ;
不详 .
Mater. Sci. Eng. A, 2 (292-299)
[47]   Analysis of steady state creep behaviour of 9-12% chromium ferritic-martensitic steels [J].
Dimmler, G ;
Weinert, P ;
Cerjak, H .
MATERIALS SCIENCE AND TECHNOLOGY, 2004, 20 (12) :1525-1530
[48]   P92钢回火工艺控制 [J].
赵强 ;
盛慧 ;
安威 ;
彭先宽 ;
徐广信 .
热加工工艺, 2016, 45 (24) :210-214+218
[49]   Warm deformation behaviour of P92 steel [J].
Obiko, J. ;
Chown, L. H. ;
Whitefield, D. J. .
MATERIALS RESEARCH EXPRESS, 2019, 6 (12)
[50]   Characterization of the creep properties of heat resistant 9-12% chromium steels by miniature specimen testing [J].
Olbricht, Juergen ;
Bismarck, Marc ;
Skrotzki, Birgit .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2013, 585 :335-342