Mechanical alloying and milling of Al-Mg alloys

被引:61
作者
Scudino, S. [1 ]
Sakaliyska, M. [1 ]
Surreddi, K. B. [1 ]
Eckert, J. [1 ,2 ]
机构
[1] IFW Dresden, Inst Komplexe Materialien, D-01171 Dresden, Germany
[2] Tech Univ Dresden, Inst Werkstoffwissensch, D-01062 Dresden, Germany
关键词
Intermetallics; Mechanical alloying; Phase transitions; Microstructure; SOLID-STATE REACTION; POWDERS; AMORPHIZATION; METALS; PHASE;
D O I
10.1016/j.jallcom.2008.07.161
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
Solid solubility extension of Mg in Al was achieved for the binary Al-Mg system in the range of 10-40 at.% Mg by mechanical alloying of elemental powder mixtures and by mechanical milling of pre-alloyed ingots. No indication for the formation of the equilibrium phases (beta-Al(3)Mg(2) and gamma-Al(12)Mg(17)) after milling was observed. The cell parameters of the solid solutions increase linearly with increasing Mg content with a slope that depends on the processing route used. During heating, the Al(Mg) solid solutions prepared from the different starting materials display a complex behavior characterized by several exothermic events. At low temperatures, an increasing amount of Mg is rejected from the solid solution with increasing temperature. At higher temperature, the beta'-phase, a hexagonal intermediate phase with approximate composition Al(3)Mg(2), is formed. The beta'-phase most likely serves as precursor for the formation of the equilibrium beta-Al(3)Mg(2) phase, which occurs in the following exothermic event. (C) 2008 Elsevier B.V. All rights reserved.
引用
收藏
页码:2 / 7
页数:6
相关论文
共 35 条
[1]  
AKHTAR D, 1987, Z METALLKD, V78, P201
[2]   Phase evolution of Mg-AI-Zr nanophase alloys prepared by mechanical alloying [J].
Al-Aqeeli, N ;
Mendoza-Suarez, G ;
Labrie, A ;
Drew, RAL .
JOURNAL OF ALLOYS AND COMPOUNDS, 2005, 400 (1-2) :96-99
[3]   MECHANICALLY DRIVEN DISORDER AND PHASE-TRANSFORMATIONS IN ALLOYS [J].
BAKKER, H ;
ZHOU, GF ;
YANG, H .
PROGRESS IN MATERIALS SCIENCE, 1995, 39 (03) :159-241
[4]   EXTENDED SOLID SOLUBILITY IN BALL-MILLED AL-MG ALLOYS [J].
CALKA, A ;
KACZMAREK, W ;
WILLIAMS, JS .
JOURNAL OF MATERIALS SCIENCE, 1993, 28 (01) :15-18
[5]   FORMATION OF QUASICRYSTALS BY MECHANICAL ALLOYING [J].
ECKERT, J ;
SCHULTZ, L ;
URBAN, K .
APPLIED PHYSICS LETTERS, 1989, 55 (02) :117-119
[6]   THERMAL-STABILITY AND GRAIN-GROWTH BEHAVIOR OF MECHANICALLY ALLOYED NANOCRYSTALLINE FE-CU ALLOYS [J].
ECKERT, J ;
HOLZER, JC ;
JOHNSON, WL .
JOURNAL OF APPLIED PHYSICS, 1993, 73 (01) :131-141
[7]   AMORPHIZATION REACTION DURING MECHANICAL ALLOYING - INFLUENCE OF THE MILLING CONDITIONS [J].
ECKERT, J ;
SCHULTZ, L ;
URBAN, K .
JOURNAL OF MATERIALS SCIENCE, 1991, 26 (02) :441-446
[8]   Mechanical alloying of highly processable glassy alloys [J].
Eckert, J .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 226 :364-373
[9]   GLASS-FORMING RANGES IN TRANSITION METAL-ZR ALLOYS PREPARED BY MECHANICAL ALLOYING [J].
ECKERT, J ;
SCHULTZ, L ;
URBAN, K .
JOURNAL OF THE LESS-COMMON METALS, 1988, 145 (1-2) :283-291
[10]   STRUCTURAL AND THERMODYNAMIC PROPERTIES OF HEAVILY MECHANICALLY DEFORMED RU AND AIRU [J].
HELLSTERN, E ;
FECHT, HJ ;
FU, Z ;
JOHNSON, WL .
JOURNAL OF APPLIED PHYSICS, 1989, 65 (01) :305-310