Effect of substrate temperature on polycrystalline Cd0.9Zn0.1Te thin films studied by Raman scattering spectroscopy

被引：17
作者：
Sridharan, M [1 ]
Mekaladevi, M
Narayandass, SK
Mangalaraj, D
Lee, HC
机构：
[1] Univ Autonoma Barcelona, Dept Fis, Grp Fis Mat 1, E-08193 Barcelona, Spain
[2] Bharathiar Univ, Dept Phys, Thin Film Lab, Coimbatore 641046, Tamil Nadu, India
[3] Korea Adv Inst Sci & Technol, Dept Elect Engn & Comp Sci, Taejon 305701, South Korea
来源：
CRYSTAL RESEARCH AND TECHNOLOGY | 2004年 / 39卷 / 04期
关键词：
Cd0.9Zn0.1Te films; vacuum evaporation; RBS; XRD; AFM; Raman scattering;
D O I：
10.1002/crat.200310190
中图分类号：
O7 [晶体学];
学科分类号：
0702 ; 070205 ; 0703 ; 080501 ;
摘要：
Cd0.9Zn0.1Te thin films were prepared by vacuum evaporation onto well-cleaned glass substrates maintained at 300, 373 and 473 K. X-ray diffraction studies revealed that the films have zinc blende structure with preferential (I 11) orientation. Raman peak of the room temperature deposited film appeared at 140.30 cm(-1) and 159.65 cm(-1) were for the transverse optic (TO) and longitudinal optic (LO) phonons respectively. The XRD patterns of the higher substrate temperature deposited films exhibited an improvement in the crystallinity of the films. The Raman peak intensity increases and the FWHM decreases for the films deposited at higher substrate temperature. (C) 2004 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim
引用
收藏
页码：328 / 332
页数：5
相关论文
共 15 条
  • [11] Sridharan M, 2002, CRYST RES TECHNOL, V37, P964, DOI 10.1002/1521-4079(200209)37:9<964::AID-CRAT964>3.0.CO
  • [12] 2-R
  • [13] DX centres in CdZnTe:Cl and their applications
    Thio, T
    Bennett, JW
    Chadi, DJ
    Linke, RA
    Becla, P
    [J]. JOURNAL OF CRYSTAL GROWTH, 1996, 159 (1-4) : 345 - 349
  • [14] LATTICE-PARAMETERS OF ZN1-XMNXSE AND TETRAHEDRAL BOND LENGTHS IN A-II-I-XMNXB-VI ALLOYS
    YODERSHORT, DR
    DEBSKA, U
    FURDYNA, JK
    [J]. JOURNAL OF APPLIED PHYSICS, 1985, 58 (11) : 4056 - 4060
  • [15] ZEMSKI VJ, 1998, SOLID STATE COMMUN, V84, P4448
12