Annealing Treatment Methods and Mechanisms for Refining Mixed and Coarse Grains in a Solution Treatment Nickel-Based Superalloy

被引:23
作者
Chen, Ming-Song [1 ,2 ]
Wang, Guan-Qiang [1 ,3 ]
Li, Hong-Bin [1 ,4 ]
Lin, Yong-Cheng [1 ,2 ,3 ]
Zou, Zong-Huai [1 ,3 ]
Ma, Yan-Yong [1 ,3 ]
机构
[1] Cent S Univ, Sch Mech & Elect Engn, Changsha 410083, Hunan, Peoples R China
[2] Cent S Univ, Light Alloy Res Inst, Changsha 410083, Hunan, Peoples R China
[3] Cent S Univ, State Key Lab High Performance Complex Mfg, Changsha 410083, Hunan, Peoples R China
[4] North China Sci & Technol Univ, Coll Met & Energy, Tangshan 063009, Peoples R China
基金
中国国家自然科学基金;
关键词
annealing treatment; homogenization; microstructural evolution; nickel-based superalloy; NI-BASED SUPERALLOY; DYNAMIC RECRYSTALLIZATION BEHAVIOR; HOT DEFORMATION-BEHAVIOR; HIGH-TEMPERATURE DEFORMATION; MICROSTRUCTURAL EVOLUTION; COMPRESSIVE DEFORMATION; GH4169; SUPERALLOY; PROCESSING MAP; FLOW-STRESS; DELTA-PHASE;
D O I
10.1002/adem.201900558
中图分类号
T [工业技术];
学科分类号
08 ;
摘要
The annealing treatment methods and mechanisms for refining deformed mixed and coarse grains in a solution treatment nickel-based superalloy are investigated. The single-stage annealing tests are done first, and it is found that the mixed and coarse grains are hardly refined to about 10 mu m by a direct annealing at 980 degrees C due to lack of delta phase. Then, two-stage annealing tests, in which the deformed sample is first heated to 900 degrees C for 12 h for precipitating some delta phases and then reheated to 980 degrees C for a recrystallization annealing treatment (RT), are designed. It is found that the recrystallization is still not complete although a long-time RT is done. The main reason is that the distances between adjacent delta phases precipitating during direct aging are so small that the recrystallization nuclei are hard to form. So, three-stage annealing tests, including a pre-recrystallization annealing treatment (PRT) at 980 degrees C, an aging annealing treatment (AT) at 900 degrees C, and an RT at 980 degrees C, are designed. It is found that the PRT has a favorable influence on the refinement of mixed and coarse grains during the subsequent AT and RT. The mixed and coarse grains can be refined after the three-stage annealing treatment of 980 degrees C x 3 min/WQ + 900 degrees C x 12 h/WQ + 980 degrees C x 120 min/WQ.
引用
收藏
页数:13
相关论文
共 62 条
[21]   Dynamic recrystallization in Mone1400 Ni-Cu alloy: Mechanism and role of twinning [J].
Ebrahimi, G. R. ;
Momeni, A. ;
Ezatpour, H. R. ;
Jahazi, M. ;
Bocher, P. .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 744 :376-385
[22]   Hot deformation behavior and constitutive model of GH4169 superalloy for linear friction welding process [J].
Geng, Peihao ;
Qin, Guoliang ;
Zhou, Jun ;
Zou, Zengda .
JOURNAL OF MANUFACTURING PROCESSES, 2018, 32 :469-481
[23]   Particle stimulated nucleation during dynamic recrystallization using a cellular automata model [J].
Goetz, RL .
SCRIPTA MATERIALIA, 2005, 52 (09) :851-856
[25]   Hall-Petch relation and boundary strengthening [J].
Hansen, N .
SCRIPTA MATERIALIA, 2004, 51 (08) :801-806
[26]   Influences of pre-precipitated 8 phase on microstructures and hot compressive deformation features of a nickel-based superalloy [J].
He, Dao-Guang ;
Lin, Y. C. ;
Wang, Li-Hua ;
Wu, Qiao ;
Zu, Zi-Heng ;
Cheng, Hao .
VACUUM, 2019, 161 :242-250
[27]   Influences of solution cooling on microstructures, mechanical properties and hot corrosion resistance of a nickel-based superalloy [J].
He, Dao-Guang ;
Lin, Y. C. ;
Tang, Yi ;
Li, Ling ;
Chen, Jian ;
Chen, Ming-Song ;
Chen, Xiao-Min .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2019, 746 :372-383
[28]   Microstructural variations and kinetic behaviors during metadynamic recrystallization in a nickel base superalloy with pre-precipitated δ phase [J].
He, Dao-Guang ;
Lin, Y. C. ;
Wang, Li-Hua .
MATERIALS & DESIGN, 2019, 165
[29]   Microstructural evolution and support vector regression model for an aged Ni-based superalloy during two-stage hot forming with stepped strain rates [J].
He, Dao-Guang ;
Lin, Y. C. ;
Chen, Jian ;
Chen, Dong-Dong ;
Huang, Jian ;
Tang, Yi ;
Chen, Ming-Song .
MATERIALS & DESIGN, 2018, 154 :51-62
[30]   Application of the finite element method to predict microstructure evolution in the hot forging of steel [J].
Jang, YS ;
Ko, DC ;
Kim, BM .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2000, 101 (1-3) :85-94