Spreading of Sn-Ag-Ti and Sn-Ag-Ti(-Al) solder droplets on the surface of porous graphite through ultrasonic vibration

被引：20
作者：
Yu, Weiyuan [1 ]
Liu, Yun [1 ]
Liu, Xinya [1 ]
机构：
[1] Lanzhou Univ Technol, State Key Lab Gansu Prov, Adv Proc & Recycling Nonferrous Met, Lanzhou 730050, Gansu, Peoples R China
来源：
MATERIALS & DESIGN | 2018年 / 150卷
基金：
中国国家自然科学基金;
关键词：
Graphite; Active solder; Spreading; Ultrasonic-assisted soldering; MICROSTRUCTURE; STORAGE; COPPER; FOAM;
D O I：
10.1016/j.matdes.2018.04.028
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The spreading process of an active solder droplet on porous graphite surface was captured by using high-speed camera. The spreading characteristics of the Sn5Ag8Ti and Sn5Ag2Ti1Al active solder under ultrasonic vibrations were analysed. The results showed that applying ultrasonicwaves during the soldering process enable the active solder to spread on the graphite surface at a relatively low temperature under atmospheric condition. Initially, the solder spread slowly on the graphite surface in the direction opposite to that of the ultrasonicwave transmission because of the rapid attenuation of ultrasonic amplitude on the surface of the graphite. Then graphite pores were rapidly filled with solder under the action of ultrasonic vibration, which prevented the ultrasonic attenuation. Subsequently, the solder spread out rapidly along the direction of transmission. In addition, the spreading distance and rate of Sn5Ag8Ti were significantly less than that of Sn5Ag2Ti1Al solder, which was determined by the composition and thickness of the oxide film on the surface of the active solder. (C) 2018 Elsevier Ltd. All rights reserved.
引用
收藏
页码：9 / 16
页数：8
相关论文
共 30 条
[1]   The use of graphite foams for simultaneous collection and storage of concentrated solar energy [J].
Badenhorst, Heinrich ;
Fox, Natasha ;
Mutalib, Ashraf .
CARBON, 2016, 99 :17-25
[2]   Spreading and atomization of droplets on a vibrating surface in a standing pressure field [J].
Deepu, P. ;
Basu, Saptarshi ;
Saha, Abhishek ;
Kumar, Ranganathan .
APPLIED PHYSICS LETTERS, 2012, 101 (14)
[3]   Friction stir soldering: A novel route to produce graphite-copper dissimilar joints [J].
Ebrahimian, A. ;
Kokabi, A. H. .
MATERIALS & DESIGN, 2017, 116 :599-608
[4]   Wettability and bonding of graphite by Sn0.3Ag0.7Cu-Ti alloys [J].
Fu, W. ;
Hu, S. P. ;
Song, X. G. ;
Li, J. X. ;
Cao, J. ;
Feng, J. C. ;
Wang, G. D. .
CARBON, 2017, 121 :536-543
[5]   Effect of Ti content on the wetting behavior of Sn0.3Ag0.7Cu/AlN system [J].
Fu, W. ;
Song, X. G. ;
Zhao, Y. X. ;
Cao, J. ;
Feng, J. C. ;
Jin, C. ;
Wang, G. D. .
MATERIALS & DESIGN, 2017, 115 :1-7
[6]  
Hafez K.M., 2002, T JWRI, V31, P177
[7]   Microstructural Evolution of Lead-Free Solder Joints in Ultrasonic-Assisted Soldering [J].
Ji, Hongjun ;
Wang, Qiang ;
Li, Mingyu .
JOURNAL OF ELECTRONIC MATERIALS, 2016, 45 (01) :88-97
[8]   Effects of ultrasonic irradiation and cooling rate on the solidification microstructure of Sn-3.0Ag-0.5Cu alloy [J].
Ji, Hongjun ;
Wang, Qiang ;
Li, Mingyu ;
Wang, Chunqing .
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2014, 214 (01) :13-20
[9]   Heat transfer analysis of a latent heat thermal energy storage system using graphite foam for concentrated solar power [J].
Kim, Taeil ;
France, David M. ;
Yu, Wenhua ;
Zhao, Weihuan ;
Singh, Dileep .
SOLAR ENERGY, 2014, 103 :438-447
[10]   Shear strength and wettability of active Sn3.5Ag4Ti(Ce,Ga) solder on Al2O3 ceramics [J].
Kolenak, R. ;
Sebo, P. ;
Provaznik, M. ;
Kolenakova, M. ;
Ulrich, K. .
MATERIALS & DESIGN, 2011, 32 (07) :3997-4003
123