Corrosion behavior of 2099 Al-Li alloy in NaCl aqueous solution

被引：12
|
作者：
Chen, Bin [1 ]
Li, Chao-Hao [1 ]
He, Shi-Chen [1 ]
Li, Xiao-ling [1 ]
Lu, Chen [1 ]
机构：
[1] Shanghai Jiao Tong Univ, Sch Mat Sci & Engn, Shanghai 200240, Peoples R China
来源：
JOURNAL OF MATERIALS RESEARCH | 2014年 / 29卷 / 12期
关键词：
CU-MG ALLOYS; PITTING CORROSION; ELECTROCHEMICAL-BEHAVIOR; ALUMINUM-ALLOY; AEROSPACE; FILMS;
D O I：
10.1557/jmr.2014.121
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The corrosion behavior of 2099 Al-Li alloy in NaCl aqueous solutions with different concentrations (1.5, 3.5, and 5.0% in mass fraction) was investigated. Its corrosion resistance was evaluated using electrochemical measurements together with full immersion tests. The results showed that the 2099 Al-Li alloy possessed good corrosion resistance in NaCl aqueous solutions. Its corrosion rate increased with increasing chloride ion concentration. The main form of corrosion failure was pitting corrosion. The impurity containing sulfur leads to surface pitting. The oxide films that formed during the manufacturing process offer a good resistance to corrosion. They are likely to suffer separation, cracking, and drop-off when immersed in aggressive NaCl aqueous solution. The good corrosion susceptibility of the alloy may be attributed to homogeneous coherent nanoscale precipitates.
引用
收藏
页码：1344 / 1353
页数：10
相关论文
共 50 条
  • [31] Microstructural influence on corrosion behavior of MgZnGe alloy in NaCl solution
    Jiang, Pingli
    Blawert, Carsten
    Hou, Ruiqing
    Scharnagl, Nico
    Bohlen, Jan
    Zheludkevich, Mikhail L.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2019, 783 : 179 - 192
  • [32] Corrosion behavior of Ti-Al-N/Ti-Al duplex coating on AZ31 magnesium alloy in NaCl aqueous solution
    Wu, Guosong
    Wang, Xuemin
    Ding, Kejian
    Zhou, Yuanyuan
    Zeng, Xiaoqin
    MATERIALS CHARACTERIZATION, 2009, 60 (08) : 803 - 807
  • [33] Corrosion behavior of 1420 Al-Li alloy under MgCl2 drops in 33% relative humidity
    Li, C. -X.
    Tan, X.
    Li, J. -F.
    Zheng, Z. -Q.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2014, 65 (05): : 476 - 484
  • [34] Effects of re-solution and re-aging treatment on mechanical property, corrosion resistance and electrochemical behavior of 2196 Al-Cu-Li alloy
    Chen, Xiaoxue
    Ma, Xinwu
    Zhao, Guoqun
    Wang, Yongxiao
    Xu, Xiao
    MATERIALS & DESIGN, 2021, 204
  • [35] Comparison of corrosion behavior of Al-Mn and Al-Mg alloys in chloride aqueous solution
    Wang, B.
    Liu, J.
    Yin, M.
    Xiao, Y.
    Wang, X. H.
    He, J. X.
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2016, 67 (01): : 51 - 59
  • [36] Effect of heat treatment on hot deformation behavior and microstructure evolution of 2195 Al-Li alloy
    Wang, Rui-qi
    Dai, Guo-qing
    Guo, Yan-hua
    Sun, Zhong-gang
    Yang, Jiao-xi
    Chang, Hui
    Liu, Chun-hui
    Alexandrov, Igor V.
    Zhan, Li-hua
    JOURNAL OF CENTRAL SOUTH UNIVERSITY, 2023, 30 (05) : 1417 - 1434
  • [37] Corrosion behavior of Al-3.0 wt%Mg alloy in NaCl solution under magnetic field
    Xin Zhang
    Ze-Hua Wang
    Ze-Hua Zhou
    Jian-Ming Xu
    Zhao-Jun Zhong
    Huan-Long Yuan
    Rare Metals, 2017, 36 (08) : 627 - 634
  • [38] Corrosion behavior of Al-3.0 wt% Mg alloy in NaCl solution under magnetic field
    Zhang, Xin
    Wang, Ze-Hua
    Zhou, Ze-Hua
    Xu, Jian-Ming
    Zhong, Zhao-Jun
    Yuan, Huan-Long
    RARE METALS, 2017, 36 (08) : 627 - 634
  • [39] Effect of aging treatment on the exfoliation corrosion and stress corrosion cracking behaviors of 2195 Al-Li alloy
    Wang, Xue-hui
    Wang, Ji-hui
    Yue, Xin
    Gao, Yun
    MATERIALS & DESIGN, 2015, 67 : 596 - 605
  • [40] The corrosion behavior of chromated AA2024 aluminum alloy in 3.5% NaCl solution
    Zhou, Yong
    Zhang, Pei
    Xiong, Jinping
    Yan, Fuan
    ANTI-CORROSION METHODS AND MATERIALS, 2019, 66 (06) : 879 - 887
12345