Effect of air entrainment on the performance of reactive MgO and PC mixes

被引：41

作者：

Ruan, S. ^{[1
]}

Unluer, C. ^{[1
]}

机构：

[1] Nanyang Technol Univ, Sch Civil & Environm Engn, 50 Nanyang Ave, Singapore 639798, Singapore

来源：

CONSTRUCTION AND BUILDING MATERIALS | 2017年 / 142卷

关键词：

Reactive MgO; Air-entrainment agent; Carbonation; Porosity; Strength; Microstructure; Thermal conductivity; LIFE-CYCLE ASSESSMENT; ACCELERATED CARBONATION; CEMENT PASTE; FLY-ASH; THERMAL-DECOMPOSITION; TRANSPORT-PROPERTIES; MAGNESIA CEMENTS; POROUS BLOCKS; HIGH-VOLUME; CO2;

D O I：

10.1016/j.conbuildmat.2017.03.068

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

This study investigated the influence of air-entraining agents (AEA) on the performance and microstructure of reactive MgO cement (RMC) samples in comparison with Portland cement (PC) samples under different water contents and curing conditions. Porosity, density, workability, strength, pH and thermal conductivity measurements were supported with XRD, TGAIDSC and SEM analyses. Performance of RMC samples depended on the dense formation of carbonate phases such as nesquehonite and hydro-magnesite, whereas PC samples gained strength by hydration. Introduction of AEA reduced early strength due to increased air contents. This was compensated by increased CO2 penetration, carbonation and strength gain in longer periods. (C) 2017 Elsevier Ltd. All rights reserved.

引用

页码：221 / 232

页数：12

共 67 条

[31] Performance of magnesia cements in pressed masonry units with natural aggregates: Production parameters optimisation [J].

Liska, M. ;

Al-Tabbaa, A. .

CONSTRUCTION AND BUILDING MATERIALS, 2008, 22 (08) :1789-1797

[32] Influence of carbonation on the properties of reactive magnesia cement-based pressed masonry units [J].

Liska, M. ;

Vandeperre, L. J. ;

Al-Tabbaa, A. .

ADVANCES IN CEMENT RESEARCH, 2008, 20 (02) :53-64

[33] Performance of magnesia cements in porous blocks in acid and magnesium environments [J].

Liska, Martin ;

Al-Tabbaa, Abir .

ADVANCES IN CEMENT RESEARCH, 2012, 24 (04) :221-232

[34] Solubility of calcium hydroxide [J].

Miller, LB ;

Witt, JC .

JOURNAL OF PHYSICAL CHEMISTRY, 1929, 33 (01) :285-289

[35]

Mo L., 2016, Journal of Cleaner Production, P1

[36] Effectiveness of using CO2 pressure to enhance the carbonation of Portland cement-fly ash-MgO mortars [J].

Mo, Liwu ;

Zhang, Feng ;

Deng, Min ;

Panesar, Daman K. .

CEMENT & CONCRETE COMPOSITES, 2016, 70 :78-85

[37] Accelerated carbonation - A potential approach to sequester CO2 in cement paste containing slag and reactive MgO [J].

Mo, Liwu ;

Panesar, Daman K. .

CEMENT & CONCRETE COMPOSITES, 2013, 43 :69-77

[38] Effects of accelerated carbonation on the microstructure of Portland cement pastes containing reactive MgO [J].

Mo, Liwu ;

Panesar, Daman K. .

CEMENT AND CONCRETE RESEARCH, 2012, 42 (06) :769-777

[39]

Neville AM, 1996, Properties of concrete

[40] Properties of binary and ternary reactive MgO mortar blends subjected to CO2 curing [J].

Panesar, Daman K. ;

Mo, Liwu .

CEMENT & CONCRETE COMPOSITES, 2013, 38 :40-49

← 1 2 3 4 5 6 7 →