Chemical Composition and Surface Roughness of AlOx-Controlled Activity of Pt/AlOx Thin Film Catalysts for Methanol Oxidation Reaction

被引：2
|
作者：
Chen, Ying [1 ,2 ]
Liu, Jun [1 ,3 ]
Wang, Xiaohong [1 ,4 ]
Wang, Wei [1 ,4 ]
Zeng, Zhigang [1 ,2 ]
Hu, Zhiyu [1 ,2 ,5 ]
机构：
[1] Shanghai Univ, Inst NanoMicroEnergy, Shanghai 200444, Peoples R China
[2] Shanghai Univ, Coll Sci, Dept Phys, Shanghai 200444, Peoples R China
[3] Shanghai Univ, Sch Mat Sci & Engn, Shanghai 200072, Peoples R China
[4] Shanghai Univ, Coll Sci, Dept Chem, Shanghai 200444, Peoples R China
[5] Shanghai Jiao Tong Univ, Dept Micro Nano Elect, Natl Key Lab Sci & Technol Micro Nano Fabricat, Shanghai 200240, Peoples R China
来源：
CATALYSIS LETTERS | 2014年 / 144卷 / 10期
基金：
中国国家自然科学基金;
关键词：
Magnetron sputtering; Pt/AlOx thin film catalyst; O-2/Ar ratio; Surface roughness; Chemisorbed Oxygen; VANADIA CATALYSTS; SPECTROSCOPY; AL2O3;
D O I：
10.1007/s10562-014-1331-4
中图分类号：
O64 [物理化学（理论化学）、化学物理学];
学科分类号：
070304 ; 081704 ;
摘要：
Chemical composition and surface roughness of AlOx films were facilely controlled by manipulating O-2/Ar ratio during aluminum oxide sputter-deposition process. Pt/AlOx catalyst synthesized with O-2/Ar ratio of 2 % exhibits the highest roughness (8.55 nm) and lowest O/Al ratio (0.11), which showed the best catalytic activity with a methanol conversion rate of 92.5 % and a remarkable temperature rise of 12 A degrees C induced by exothermic reaction at 100 A degrees C. It was demonstrated that Pt/AlOx catalysts had significant higher activity for methanol oxidation when the AlOx was nonstoichiometric compared with its stoichiometric counterpart (Al2O3). The outstanding catalytic performance and novel nanostructure of the deposited Pt/AlOx thin film catalyst endow it with great potential for developing next-generation energy conversion devices and combustible gas sensors.
引用
收藏
页码：1696 / 1703
页数：8
相关论文
共 37 条
  • [31] Preparation of a Pt thin-film modified electrode for alkaline electrocatalytic oxidation of methanol by Cu(OH)2 electrodeposition and galvanic replacement reaction
    Zhang, Chunxiu
    Chao, Long
    Wang, Linping
    Cheng, Yan
    Xie, Qingji
    ELECTROCHIMICA ACTA, 2020, 330
  • [32] Electrocatalytic activity and stability of carbon nanotubes-supported Pt-on-Au, Pd-on-Au, Pt-on-Pd-on-Au, Pt-on-Pd, and Pd-on-Pt catalysts for methanol oxidation reaction
    Shi, Ranran
    Wang, Jianshe
    Cheng, Niancai
    Sun, Xueliang
    Zhang, Lei
    Zhang, Jiujun
    Wang, Liucheng
    ELECTROCHIMICA ACTA, 2014, 148 : 1 - 7
  • [33] Role of Chemical Composition in the Enhanced Catalytic Activity of Pt-Based Alloyed Ultrathin Nanowires for the Hydrogen Oxidation Reaction under Alkaline Conditions
    Scofield, Megan E.
    Zhou, Yuchen
    Yue, Shiyu
    Wang, Lei
    Su, Dong
    Tong, Xiao
    Vukmirovic, Miomir B.
    Adzic, Radoslav R.
    Wong, Stanislaus S.
    ACS CATALYSIS, 2016, 6 (06): : 3895 - 3908
  • [34] Oxygen Reduction Reaction Activity for Strain-Controlled Pt-Based Model Alloy Catalysts: Surface Strains and Direct Electronic Effects Induced by Alloying Elements
    Asano, Masato
    Kawamura, Ryutaro
    Sasakawa, Ren
    Todoroki, Naoto
    Wadayama, Toshimasa
    ACS CATALYSIS, 2016, 6 (08): : 5285 - 5289
  • [35] Oxidative addition of 1,4-dichloro-2-butyne to an organoplatinum complex: A new precursor for synthesis of ultrasmall Pt nanoparticles thin film at liquid/liquid interface as the electrocatalyst in methanol oxidation reaction
    Sadri, Nazanin
    Hoseini, S. Jafar
    APPLIED ORGANOMETALLIC CHEMISTRY, 2019, 33 (09)
  • [36] Structure-activity correlations in thin film model catalysts:: CO hydrogenation on Rh/VOx -: Part I.: The morphology, composition and structure of vanadia-supported and -promoted Rh particles upon oxidation and reduction
    Penner, Simon
    Jenewein, Bernd
    Wang, Di
    Schloegl, Robert
    Hayek, Konrad
    APPLIED CATALYSIS A-GENERAL, 2006, 308 : 31 - 42
  • [37] Effects of Metal Promoters (M = Fe, Co, and Cu) in Pt/Mx Zry Oz Catalysts and Influence of CO2 and H2O on the CO Oxidation Activity (PROX): Analysis of Surface Properties After Reaction
    Gaioto, Carolina C.
    Pinto, Jose Carlos
    Schmal, Martin
    ACS OMEGA, 2024, 9 (24): : 25715 - 25729
1234