Corrosion behavior of TLP bonded stainless steel 304 with Ni-based interlayer

被引：22

作者：

Kazazi, Arash ^{[1
]}

Ekrami, Aliakbar ^{[1
]}

机构：

[1] Sharif Univ Technol, Dept Mat Sci & Engn, Tehran, Iran

来源：

JOURNAL OF MANUFACTURING PROCESSES | 2019年 / 42卷

关键词：

Transient liquid phase bonding; 304 Stainless steel; Ni-based interlayer; Corrosion behavior; Oxidation; TRANSIENT LIQUID-PHASE; MICROSTRUCTURAL EVOLUTION; SUPERALLOY; 304-STAINLESS-STEEL; TEMPERATURE; RESISTANCE; OXIDATION; JOINTS;

D O I：

10.1016/j.jmapro.2019.04.029

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

Transient liquid phase bonding of AISI 304 was carried out in a vacuum furnace using a Ni-based interlayer. The effect of bonding time on microstructure and mechanical properties of joints made at temperature of 1150 degrees C was investigated. The results showed that isothermal solidification was completed within 20 min and the eutectic phase disappeared across the joint region. The joints with complete isothermal solidification were homogenized for 180 min at a temperature of 950 degrees C. The shear test results showed that the average shear strength of the homogenized samples was about 83% of that of the base metal at the same heat treatment cycle. Corrosion behavior of the TLP-bonded samples and the base metal was studied at 23 degrees C in 3.5% NaCl and 10% H2SO4 solutions. Corrosion resistance of TLP bonded was lower than that of the base metal, but the homo-genizing treatment increased the corrosion resistance of the bonded samples. Isothermal thermogravimetric curves of both the TLP-bonded sample and the base metal were plotted. The weight gains of TLP-bonded in a period of 120 h was greater than that of the base metal at 925 degrees C.

引用

页码：131 / 138

页数：8

共 43 条

[1] The effect of bonding time on the microstructure and mechanical properties of transient liquid phase bonding between SAF 2507 and AISI 304 [J].

Abdolvand, R. ;

Atapour, M. ;

Shamanian, M. ;

Allafchian, A. .

JOURNAL OF MANUFACTURING PROCESSES, 2017, 25 :172-180

[2] Enhanced Corrosion Resistance of a Transient Liquid Phase Bonded Nickel-Based Superalloy [J].

Adebajo, O. J. ;

Ojo, O. A. .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 2017, 48A (01) :26-33

[3]

[Anonymous], 1996, E11213 AS, P4

[4]

[Anonymous], 2012, Standard Test Methods for Tension Testing of Metallic Materials, DOI 10.1520/F2792-12A

[5]

[Anonymous], 2009, ANN BOOK ASTM STAND, P237

[6] The joint properties of a high-chromium Ni-based superalloy made by diffusion brazing: Microstructural evolution, corrosion resistance and mechanical behavior [J].

Arhami, Farzam ;

Mirsalehi, Seyyed Ehsan ;

Sadeghian, Amirhossein ;

Johar, Mohammad Hossein .

JOURNAL OF MANUFACTURING PROCESSES, 2019, 37 :203-211

[7] Evidence for chromium evaporation influencing the oxidation of 304L: The effect of temperature and flow rate [J].

Asteman, H ;

Svensson, JE ;

Johansson, LG .

OXIDATION OF METALS, 2002, 57 (3-4) :193-216

[8]

Atabaki MM, 2013, WELD J, V92, p57S

[9]

Baker H., 1992, ALLOY PHASE DIAGRAMS, V3, P2

[10] Effect of configuration and composition of interlayer on TLP joints of FSX-414 superalloy [J].

Bakhtiari, R. .

JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2016, 231 :8-17

← 1 2 3 4 5 →