Thermal residual stresses effects on fatigue crack growth of repaired panels bounded with various composite materials

被引：38

作者：

Hosseini-Toudeshky, Hossein ^{[1
]}

Mohammadi, Bijan

机构：

[1] Amir Kabir Univ Technol, Dept Aerosp Engn, Tehran, Iran

来源：

COMPOSITE STRUCTURES | 2009年 / 89卷 / 02期

关键词：

Repair; Aluminum panels; Composite; Thermal; Residual stresses; ALUMINUM PANELS; PATCHES; PLATE;

D O I：

10.1016/j.compstruct.2008.07.029

中图分类号：

O3 [力学];

学科分类号：

08 ; 0801 ;

摘要：

Thermal residual stresses. due to the curing cycle of the bonded composite patch affects the stress/strain states and the crack patching efficiency of the single-side repaired aluminum panels. In this study the thermal residual stresses that occur as a result of the thermal expansion coefficient mismatch between the patch and the underlying cracked aluminum panel are investigated. The fatigue crack-growth life and the crack-front configuration of centrally cricked aluminum panels in mode-I condition with various single-side repairs of glass/epoxy, graphite/epoxy and boron/epoxy composite patches are curried out. Sensitivity of the obtained residual stresses to different curing temperatures of the repaired panels with various composite patches is also investigated. It is shown that low curing temperatures (e.g., 60 degrees C) with long curing cycles have not a considerable effect on fatigue crack-growth life of the repaired panels with glass/epoxy patch and have minor effects for repaired panels with graphite/epoxy and boron/epoxy composite patches. It is also shown that considering the thermal residual stresses, the obtained FEM fatigue life and crack-front shapes of the repaired panels using glass/epoxy patch are in good agreement with those obtained from the experiments. (C) 2008 Elsevier Ltd. All rights reserved.

引用

页码：216 / 223

页数：8

共 21 条

[1]

Baker A.A., 1988, Bonded repair of aircraft structures

[2]

BAKER AA, 2002, ADV BONDED COMPOSITE, pCH13

[3] Composite patch repairs of metal structures: Adhesive nonlinearity, thermal cycling, and debonding [J].

Chow, WT ;

Atluri, SN .

AIAA JOURNAL, 1997, 35 (09) :1528-1535

[4]

CROOKS HR, 2003, THESIS AIR FORCE I T

[5] An analytical estimate of thermal effects in a composite bonded repair: plane stress analysis [J].

Duong, CN ;

Yu, J .

INTERNATIONAL JOURNAL OF SOLIDS AND STRUCTURES, 2002, 39 (04) :1003-1014

[6]

Farahmand B., 1997, FATIGUE FRACTURE MEC

[7] Numerical and experimental fatigue crack growth analysis in mode-I for repaired aluminum panels using composite material [J].

Hosseini-Toudeshky, H. ;

Mohammadi, B. ;

Sadeghi, G. ;

Daghyani, H. R. .

COMPOSITES PART A-APPLIED SCIENCE AND MANUFACTURING, 2007, 38 (04) :1141-1148

[8] Mixed-mode fatigue crack growth of thin aluminium panels with single-side repair using experimental and numerical methods [J].

Hosseini-Toudeshky, H. ;

Mohammadi, B. ;

Bakhshandeh, S. .

FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2007, 30 (07) :629-639

[9] Analysis of composite skin/stiffener debounding and failure under uniaxial loading [J].

Hosseini-Toudeshky, H. ;

Mohammadi, B. ;

Hamidi, B. ;

Ovesy, H. R. .

COMPOSITE STRUCTURES, 2006, 75 (1-4) :428-436

[10] Experimental fatigue crack growth and crack-front shape analysis of asymmetric repaired aluminium panels with glass/epoxy composite patches [J].

Hosseini-Toudeshky, H ;

Sadeghi, G ;

Daghyani, HR .

COMPOSITE STRUCTURES, 2005, 71 (3-4) :401-406

← 1 2 3 →