Synthesis and characterization of whisker-shaped MnO2 nanostructure at room temperature

被引：136

作者：

Jaganyi, Deogratius ^{[1
]}

Altaf, Mohammad ^{[1
]}

Wekesa, Isaac ^{[1
]}

机构：

[1] Univ KwaZulu Natal, Sch Chem & Phys Sci, Fac Sci & Agr, Private Bag X01, ZA-3209 Pietermaritzburg, South Africa

来源：

APPLIED NANOSCIENCE | 2013年 / 3卷 / 04期

关键词：

Manganese dioxide nanoparticle; FT-IR; TEM;

D O I：

10.1007/s13204-012-0135-3

中图分类号：

TB3 [工程材料学];

学科分类号：

0805 ; 080502 ;

摘要：

Manganese dioxide nanoparticles have been synthesized, via a facile one-step solution phase approach, by the reduction of potassium permanganate with sodium thiosulphate at room temperature. Upon addition of thiosulphate to the solution of permanganate, a transparent dark-brown color species appeared which was stable for several months. The obtained MnO2 solution was characterized by means of UV-vis spectra, Transmission electron microscopy (TEM), and Fourier transforms infrared spectroscopy. Fourier transforms infrared spectroscopy spectra of pure MnO2 show the occurrence of O-Mn-O vibrational mode at around 600 and 475 cm(-1). The chemical composition was obtained by EDX analysis and confirmed the presence of Mn and O in the sample. From the TEM image, the surface morphology of the sample shows uniformly dispersed particles, which are spherical in shape. The selected area electron diffraction patterns revealed that the MnO2 are crystalline in nature.

引用

页码：329 / 333

页数：5

共 46 条

[1]

Akram M, 2007, INDIAN J CHEM A, V46, P1427

[2] Oxidative degradation of dipeptide (glycyl-glycine) by water-soluble colloidal manganese dioxide in the aqueous and micellar media [J].

Akram, Mohd ;

Kabir-ud-Din, Mohammad Altaf .

COLLOIDS AND SURFACES B-BIOINTERFACES, 2011, 82 (01) :217-223

[3] Water-soluble colloidal manganese dioxide as an oxidant for L-tyrosine in the absence and presence of non-ionic surfactant TX-100 [J].

Altaf, Mohammad ;

Akram, Mohd. ;

Kabir-ud-Din .

COLLOIDS AND SURFACES B-BIOINTERFACES, 2009, 73 (02) :308-314

[4]

Anderson ML, 2002, NANO LETT, V2, P235, DOI 10.1021/n1015707d

[5] Nanoscale colloidal metals and alloys stabilized by solvents and surfactants - Preparation and use as catalyst precursors [J].

Bonnemann, H ;

Braun, G ;

Brijoux, W ;

Brinkmann, R ;

Tilling, AS ;

Seevogel, K ;

Siepen, K .

JOURNAL OF ORGANOMETALLIC CHEMISTRY, 1996, 520 (1-2) :143-162

[6]

Bonnemann H, 2002, SYNTH METHODS ORGANO, V10, P209

[7] Study of nickel catalysts supported on silica of low surface area and prepared by reduction of nickel acetate in aqueous hydrazine [J].

Boudjahem, AG ;

Monteverdi, S ;

Mercy, M ;

Bettahar, MM .

JOURNAL OF CATALYSIS, 2004, 221 (02) :325-334

[8]

Bradley J.S., 1994, CLUSTERS COLLOIDS, P459, DOI DOI 10.1002/9783527616077.CH6

[9] Electron microscopy and catalytic study of silver catalysts: Structure sensitivity of the hydrogenation of crotonaldehyde [J].

Claus, P ;

Hofmeister, H .

JOURNAL OF PHYSICAL CHEMISTRY B, 1999, 103 (14) :2766-2775

[10]

Duff DG, 1995, STUD SURF SCI CATAL, V91, P505

← 1 2 3 4 5 →