An assessment of microstructure, mechanical properties and corrosion resistance of dissimilar welds between Inconel 718 and 310S austenitic stainless steel

被引：179

作者：

Mortezaie, A. ^{[1
]}

Shamanian, M. ^{[2
]}

机构：

[1] Islamic Azad Univ, Najafabad Branch, Dept Mat Engn, Esfahan, Iran

[2] Isfahan Univ Technol, Dept Mat Engn, Esfahan 8415683111, Iran

来源：

INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING | 2014年 / 116卷

关键词：

Nickel base alloy; Austenitic stainless steel; Dissimilar materials joints; JOINT;

D O I：

10.1016/j.ijpvp.2014.01.002

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In the present study, dissimilar welding between Inconel 718 nickel-base superalloy and 310S austenitic stainless steel using gas tungsten arc welding process was performed to determine the relationship between the microstructure of the welds and the resultant mechanical and corrosion properties. For this purpose, three filler metals including Inconel 625, Inconel 82 and 310 stainless steel were used. Microstructural observations showed that weld microstructures for all filler metals were fully austenitic. In tension tests, welds produced by Inconel 625 and 310 filler metals displayed the highest and the lowest ultimate tensile strength, respectively. The results of Charpy impact tests indicated that the maximum fracture energy was related to Inconel 82 weld metal. According to the potentiodynamic polarization test results, Inconel 82 exhibited the highest corrosion resistance among all tested filler metals. Finally, it was concluded that for the dissimilar welding between Inconel 718 and 310S, Inconel 82 filler metal offers the optimum properties at room temperature. (C) 2014 Elsevier Ltd. All rights reserved.

引用

页码：37 / 46

页数：10

共 29 条

[21] The effect of rejuvenation heat treatments on the repair weldability of wrought Alloy 718 [J].

Qian, M ;

Lippold, JC .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2003, 340 (1-2) :225-231

[22] Effect of filler materials on the performance of gas tungsten arc welded AISI 304 and Monel 400 [J].

Ramkumar, K. Devendranath ;

Arivazhagan, N. ;

Narayanan, S. .

MATERIALS & DESIGN, 2012, 40 :70-79

[23] HEAT-AFFECTED ZONE CRACKING IN CAST INCONEL-718 [J].

RICHARDS, NL ;

HUANG, X ;

CHATURVEDI, MC .

MATERIALS CHARACTERIZATION, 1992, 28 (03) :179-187

[24] Microstructural features of dissimilar welds between 316LN austenitic stainless steel and alloy 800 [J].

Sireesha, M ;

Shankar, V ;

Albert, SK ;

Sundaresan, S .

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2000, 292 (01) :74-82

[25] A comparative evaluation of welding consumables for dissimilar welds between 316LN austenitic stainless steel and Alloy 800 [J].

Sireesha, M ;

Albert, SK ;

Shankar, V ;

Sundaresan, S .

JOURNAL OF NUCLEAR MATERIALS, 2000, 279 (01) :65-76

[26] Microstructural changes and corrosion resistance of AISI 310S steel exposed to 600-800°C [J].

Tavares, S. S. M. ;

Moura, V. ;

da Costa, V. C. ;

Ferreira, M. L. R. ;

Pardal, J. M. .

MATERIALS CHARACTERIZATION, 2009, 60 (06) :573-578

[27]

THOMPSON RG, 1986, WELD J, V65, pS299

[28] Characterization of microstructure, mechanical properties and corrosion resistance of dissimilar welded joint between 2205 duplex stainless steel and 16MnR [J].

Wang, Shaogang ;

Ma, Qihui ;

Li, Yan .

MATERIALS & DESIGN, 2011, 32 (02) :831-837

[29]

Winegard W. C., 1964, An Introduction to the Solidification of Metals

← 1 2 3 →