An assessment of microstructure, mechanical properties and corrosion resistance of dissimilar welds between Inconel 718 and 310S austenitic stainless steel

被引：179

作者：

Mortezaie, A. ^{[1
]}

Shamanian, M. ^{[2
]}

机构：

[1] Islamic Azad Univ, Najafabad Branch, Dept Mat Engn, Esfahan, Iran

[2] Isfahan Univ Technol, Dept Mat Engn, Esfahan 8415683111, Iran

来源：

INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING | 2014年 / 116卷

关键词：

Nickel base alloy; Austenitic stainless steel; Dissimilar materials joints; JOINT;

D O I：

10.1016/j.ijpvp.2014.01.002

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In the present study, dissimilar welding between Inconel 718 nickel-base superalloy and 310S austenitic stainless steel using gas tungsten arc welding process was performed to determine the relationship between the microstructure of the welds and the resultant mechanical and corrosion properties. For this purpose, three filler metals including Inconel 625, Inconel 82 and 310 stainless steel were used. Microstructural observations showed that weld microstructures for all filler metals were fully austenitic. In tension tests, welds produced by Inconel 625 and 310 filler metals displayed the highest and the lowest ultimate tensile strength, respectively. The results of Charpy impact tests indicated that the maximum fracture energy was related to Inconel 82 weld metal. According to the potentiodynamic polarization test results, Inconel 82 exhibited the highest corrosion resistance among all tested filler metals. Finally, it was concluded that for the dissimilar welding between Inconel 718 and 310S, Inconel 82 filler metal offers the optimum properties at room temperature. (C) 2014 Elsevier Ltd. All rights reserved.

引用

页码：37 / 46

页数：10

共 29 条

[1]

[Anonymous], 2003, WELD J

[2]

[Anonymous], 2002, ASM HDB, V1

[3]

[Anonymous], 2006, WELD HDB

[4] Delta phase precipitation in Inconel 718 [J].

Azadian, S ;

Wei, LY ;

Warren, R .

MATERIALS CHARACTERIZATION, 2004, 53 (01) :7-16

[5] Dilution and microsegregation in dissimilar metal welds between super austenitic stainless steel and nickel base alloys [J].

Banovic, SW ;

DuPont, JN ;

Marder, AR .

SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2002, 7 (06) :374-383

[6] Fibre laser welding of dissimilar alloys of Ti-6Al-4V and Inconel 718 for aerospace applications [J].

Chen, Hui-Chi ;

Pinkerton, Andrew J. ;

Li, Lin .

INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2011, 52 (9-12) :977-987

[7] Melting and solidification study of Alloy 625 [J].

Cieslak, M.J. ;

Headley, T.J. ;

Kollie, T. ;

Romig Jr., A.D. .

Metallurgical transactions. A, Physical metallurgy and materials science, 1988, 19 A (09) :2319-2331

[8] Microstructural characterization of dissimilar welds between alloy 800 and HP heat-resistant steel [J].

Dehmolaei, R. ;

Shamanian, M. ;

Kermanpur, A. .

MATERIALS CHARACTERIZATION, 2008, 59 (10) :1447-1454

[9]

Dupont J.N., 2003, WELDING RES WELDING, V82, p125s

[10] Solidification of Nb-bearing superalloys: Part II. Pseudoternary solidification surfaces [J].

DuPont, JN ;

Robino, CV ;

Marder, AR ;

Notis, MR .

METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1998, 29 (11) :2797-2806

← 1 2 3 →