Phase evolution during post-annealing and its influence on critical currents of (Bi,Pb)-2223/Ag tapes

被引：29
作者：
Qu, T. -M.
Han, Z.
Fluekiger, R.
机构：
[1] Tsing Hua Univ, Appl Superconduct Res Ctr, Dept Phys, Beijing 100084, Peoples R China
[2] Univ Geneva, Dept Appl Phys, GAP, CH-1211 Geneva, Switzerland
来源：
PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS | 2006年 / 444卷 / 1-2期
关键词：
Bi-2223/Ag tape; post-annealing; 3321; phase; critical current; n value;
D O I：
10.1016/j.physc.2006.06.001
中图分类号：
O59 [应用物理学];
学科分类号：
摘要：
Post-annealing (PA) has been performed on fully reacted multifilamentary (Bi,Pb)-2223/Ag tapes in 8.5% O-2 atmosphere. The tapes were sintered within 770-800 degrees C for 10 h and at 795 degrees C for 5-50 h. The measurements showed that I-c (77 K,SF) was increased by 12-19% after PA within 790-800 degrees C. It was found by means of XRD that the Pb-3(Bi0.5Sr2.5)Ca2CuOx (3321) phase appeared after PA, its amount decreasing with increasing PA temperature. There was an optimum 3321 content to achieve the maximum I-c. T-c was increased by PA, and then decreased with increasing temperature. The field dependent I-c and n value measurements performed at 4.2 K, 10 K, 30 K and 77 K suggested that PA improves grain connectivity and collective flux pinning. (c) 2006 Elsevier B.V. All rights reserved.
引用
收藏
页码：71 / 76
页数：6
相关论文
共 20 条
  • [1] Microstructural evolution of Bi-2223/Ag tapes during the cooling process after the first heat treatment
    Chen, XP
    Li, MY
    Qu, TM
    Liu, Q
    Han, Z
    [J]. SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 2003, 16 (10) : 1162 - 1166
  • [2] Phase formation and critical current density in Bi,Pb(2223) tapes
    Flukiger, R
    Grasso, G
    Grivel, JC
    Marti, F
    Dhalle, M
    Huang, Y
    [J]. SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1997, 10 (7A) : A68 - A92
  • [3] RAPID ANNEALING EFFECT IN THE SUPERCONDUCTING 2223 BI(PB)SRCACUO THIN-FILMS PREPARED BY SPUTTERING
    HAKURAKU, Y
    MORI, Z
    [J]. JOURNAL OF APPLIED PHYSICS, 1993, 73 (01) : 309 - 315
  • [4] HUANG YB, 2002, ADV CRYOGEN ENG, V48, P717
  • [5] BI,PB(2212) AND BI(2223) FORMATION IN THE BI-PB-SR-CA-CU-O SYSTEM
    JEREMIE, A
    ALAMIYADRI, K
    GRIVEL, JC
    FLUKIGER, R
    [J]. SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1993, 6 (10) : 730 - 735
  • [6] Critical current limiting factors in post annealed (Bi, Pb)2Sr2Ca2Cu3Ox tapes
    Jiang, J
    Cai, XY
    Chandler, JG
    Patnaik, S
    Polyanskii, AA
    Yuan, Y
    Hellstrom, EE
    Larbalestier, DC
    [J]. IEEE TRANSACTIONS ON APPLIED SUPERCONDUCTIVITY, 2003, 13 (02) : 3018 - 3021
  • [7] Controlled over-pressure sintering process of Bi2223 wires
    Kobayashi, S
    Yamazaki, K
    Kato, T
    Ohkura, K
    Ueno, E
    Fujino, K
    Fujikami, J
    Ayal, N
    Kikuchi, M
    Hayashi, K
    Sato, K
    Hata, R
    [J]. PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2005, 426 : 1132 - 1137
  • [8] Relation between critical current and exponent n in Bi(2223)/Ag tapes
    Kovac, P
    Cesnak, L
    Melisek, T
    Husek, I
    Frohlich, K
    [J]. SUPERCONDUCTOR SCIENCE & TECHNOLOGY, 1997, 10 (08) : 605 - 611
  • [9] LARBALESTIER DC, 1999, ADV SUPERCONDUCTIVIT, V11, P14520
  • [10] Effect of post-annealing on critical current density of (Bi,Pb)-2223/Ag tapes
    Li, MY
    Chen, XP
    Qu, TM
    Yi, HP
    Han, Z
    Liu, Q
    [J]. PHYSICA C-SUPERCONDUCTIVITY AND ITS APPLICATIONS, 2004, 412 : 1091 - 1095
12