Magnesium Removal from Liquors of Laterite Leaching

被引：0
|
作者：
Liu, Kui [1 ]
Chen, Xingxin [1 ]
机构：
[1] Guangxi Normal Univ, Sch Chem & Chem Engn, Guilin 541004, Peoples R China
来源：
ADVANCES IN ENVIRONMENTAL TECHNOLOGIES, PTS 1-6 | 2013年 / 726-731卷
关键词：
basic magnesium carbonate; magnesium carbonate; magnesium hydrate; magnesium removal temperature; NICKEL;
D O I：
10.4028/www.scientific.net/AMR.726-731.2206
中图分类号：
X [环境科学、安全科学];
学科分类号：
08 ; 0830 ;
摘要：
In this study, magnesium removal through reaction of alkaline liquors and magnesium cation in liquors of laterite leaching was investigated. Basic magnesium carbonate and magnesium carbonate with high filtration properties were obtained at 70 degrees C or above, whereas magnesium hydrate colloid existed in the products at temperatures below 70 degrees C, resulting in the difficulty of product filtration. When the molar ratio of Na2CO3 to Mg2+ was 2.25:1, the reaction temperature was 90-100 degrees C and the reaction time was 30min, nearly 100% magnesium was removed from liquors.
引用
收藏
页码：2206 / 2209
页数：4
相关论文
共 50 条
  • [1] Removal of Mn(II) from hydrochloric acid leach liquors of nickel laterite ore through microbubble oxidation and acid leaching
    Xu, Ziyang
    Wei, Guangye
    Yu, Zhihui
    Meng, Long
    Zheng, Shili
    Qu, Jingkui
    Qi, Tao
    HYDROMETALLURGY, 2022, 210
  • [2] Synthesis of Magnesium Hydroxide Submicroplatelets from Laterite Leaching Solutions
    Gao, Jian-ming
    Zhang, Mei
    Guo, Min
    CHEMISTRY LETTERS, 2014, 43 (09) : 1508 - 1510
  • [3] Study on Leaching of High-Magnesium Laterite
    Kuang, Lifang
    Tan, Junyue
    Liu, Kui
    PROCEEDINGS OF THE 2016 5TH INTERNATIONAL CONFERENCE ON ENERGY AND ENVIRONMENTAL PROTECTION (ICEEP 2016), 2016, 98 : 298 - 301
  • [4] Removal of magnesium from nickel laterite leach liquors by chemical precipitation using calcium hydroxide and the potential use of the precipitate as a filler material
    Karidakis, T
    Agatzini-Leonardou, S
    Neou-Syngouna, P
    HYDROMETALLURGY, 2005, 76 (1-2) : 105 - 114
  • [5] Effect of Magnesium on Pressure Leaching of Moa Laterite Ore
    Chalkley, M. E.
    Collins, M. J.
    Iglesias, C.
    Tuffrey, N. E.
    CANADIAN METALLURGICAL QUARTERLY, 2010, 49 (03) : 227 - 234
  • [6] Leaching of magnesium from desiliconization slag of nickel laterite ores by carbonation process
    牟文宁
    翟玉春
    刘岩
    Transactions of Nonferrous Metals Society of China, 2010, 20(S1) (S1) : 87 - 91
  • [7] Leaching of magnesium from desiliconization slag of nickel laterite ores by carbonation process
    Mu Wen-ning
    Zhai Yu-chun
    Liu Yan
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2010, 20 : S87 - S91
  • [8] Removal of organic substances from Bayer process liquors by magnesium compounds
    Zaytsev, YA
    Lipin, VA
    LIGHT METALS 1998, 1998, : 97 - 101
  • [9] The carbothermic reduction process for magnesium removal from nickel laterite in vacuum
    Xu B.
    Pei H.
    Yang B.
    Liu D.
    Qu T.
    Dai Y.
    Zhenkong Kexue yu Jishu Xuebao/Journal of Vacuum Science and Technology, 2011, 31 (03): : 341 - 347
  • [10] Aluminum Removal from Leach Liquor of Nitric Acid Pressure Leaching Laterite Ores
    Ma, Baozhong
    Wang, Chengyan
    Yang, Weijiao
    Yin, Fei
    Chen, Yongqiang
    ADVANCES IN CHEMICAL, MATERIAL AND METALLURGICAL ENGINEERING, PTS 1-5, 2013, 634-638 : 3191 - 3195
12345