Creep rupture properties of HAZs of a high Cr ferritic steel simulated by a weld simulator

被引：51

作者：

Albert, SK ^{[1
]}

Matsui, M ^{[1
]}

Hongo, H ^{[1
]}

Watanabe, T ^{[1
]}

Kubo, K ^{[1
]}

Tabuchi, M ^{[1
]}

机构：

[1] Natl Inst Mat Sci, Mat Informat Technol Stn, High Temp Mat Grp, Tsukuba, Ibaraki 3050047, Japan

来源：

INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING | 2004年 / 81卷 / 03期

基金：

日本学术振兴会;

关键词：

creep; type IV cracking; high Cr ferritic steel; heat affected zone simulation; finite element method analysis;

D O I：

10.1016/j.ijpvp.2004.01.003

中图分类号：

T [工业技术];

学科分类号：

08 ;

摘要：

In this work, creep rupture properties of the heat affected zones (HAZs) of P122 steel, simulated by employing a weldsimulator are studied and the results are compared with those of HAZs simulated by heat treatment. Microstructures corresponding to intercritical HAZ, fine-grained HAZ and coarse-,gained HAZ (CGHAZ) were produced using a weld simulator in the middle of specimens. These specimens were then subjected to heat treatment equivalent to post weld heat treatment and the creep specimens machined from them were tested at 923 K at three stress levels. Results showed that, irrespective of the peak temperature of simulation, fracture always occurred in that part of the specimens heated to the temperature close to Ac-3 during simulation, which was found to have a fine grain structure and minimum creep strength. However. in specimens with temperatures of simulation above Ac-3. creep cavities were observed and for those with a 1473 K simulation temperature. fracture occurred with very low ductility as observed in actual weld joints. Stress and strain distributions within the specimen during creep deformation were analyzed using the finite element method. The results indicate that creep deformation and fracture are influenced by the multiaxial stress state produced in the specimen due to the existence of different microstructures varying significantly in their creep properties. Results also suggest that the creep tests using specimens with CGHAZ microstructures simulated at the centre can successfully produce a creep fracture similar to the Type IV fracture that is observed in ferritic steel weld joints. (C) 2004 Elsevier Ltd. All rights reserved.

引用

页码：221 / 234

页数：14

共 23 条

[1]

AKKER WT, 2001, P 3 C ADV MAT TECHN, P3

[2] Variation in the Type IV cracking behaviour of a high Cr steel weld with post weld heat treatment [J].

Albert, SK ;

Matsui, M ;

Watanabe, T ;

Hongo, H ;

Kubo, K ;

Tabuchi, M .

INTERNATIONAL JOURNAL OF PRESSURE VESSELS AND PIPING, 2003, 80 (06) :405-413

[3] Microstructural investigations on Type IV cracking in a high Cr steel [J].

Albert, SK ;

Matsui, M ;

Watanabe, T ;

Hongo, H ;

Kubo, K ;

Tabuchi, M .

ISIJ INTERNATIONAL, 2002, 42 (12) :1497-1504

[4]

BELL K, 1997, 5971997 WELD I

[5]

Bendick W, 1999, ADVANCED HEAT RESISTANT STEELS FOR POWER GENERATION, P133

[6]

ELLIS FV, 1998, REV TYPE 4 CRACKING, P125

[7] NUCLEATION OF CAVITIES BY PLASTIC-DEFORMATION - OVERVIEW [J].

GOODS, SH ;

BROWN, LM .

ACTA METALLURGICA, 1979, 27 (01) :1-15

[8]

Hasegawa Y., 2001, P 3 C ADV MAT TECHN, P457

[9] THE GROWTH OF GRAIN-BOUNDARY VOIDS UNDER STRESS [J].

HULL, D ;

RIMMER, DE .

PHILOSOPHICAL MAGAZINE, 1959, 4 (42) :673-687

[10] Micromechanism of ductile crack initiation in structural steels based on void nucleation and growth [J].

Ishikawa, N ;

Parks, DM ;

Kurihara, M .

ISIJ INTERNATIONAL, 2000, 40 (05) :519-527

← 1 2 3 →