Inducing very high cycle fretting-fatigue in the ultrasonic regime

被引：11
|
作者：
Filgueiras, Pedro F. [2 ]
Bathias, Claude [1 ]
Palma, Ernani S. [2 ]
Wang, Chong [1 ]
机构：
[1] Univ Paris Ouest, Lab Energet Mecan Electromagnetisme, F-92410 Yule Davray, France
[2] Univ Fed Minas Gerais, Dept Mech Engn, BR-31270901 Belo Horizonte, MG, Brazil
来源：
TRIBOLOGY INTERNATIONAL | 2014年 / 76卷
关键词：
Fretting; Very high cycle fatigue; Ultrasonic testing; Fatigue damage; STEEL;
D O I：
10.1016/j.triboint.2013.10.023
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Early crack initiation due to fretting may have an important role in fatigue strength of steel components, mainly in the very high-cycle regime, i.e., beyond a million cycles. This work aimed to induce very high-cycle fretting-fatigue on a medium strength steel alloy in the ultrasonic regime. Specimens were subjected to push-pull fatigue and 10 mu m-amplitude fretting with crossed cylinders configuration. The normal load was held constant at 30 N. Results showed a knockdown factor of 1.5 for the fatigue strength in the fretting condition under study. The average diameter of the fretted surfaces was found to linearly increase with decreasing axial bulk stress amplitude. (C) 2014 Elsevier Ltd. All rights reserved.
引用
收藏
页码：57 / 62
页数：6
相关论文
共 50 条
  • [41] Fatigue behaviour of reinforcing steel in the very-high-cycle-fatigue regime N ≥ 10 millions
    Rappl, Stefan
    Osterminski, Kai
    Ansary, Shima
    Hiemer, Florian
    BETON- UND STAHLBETONBAU, 2021, 116 (03) : 232 - 239
  • [42] Very high cycle fatigue - Is there a fatigue limit?
    Pyttel, B.
    Schwerdt, D.
    Berger, C.
    INTERNATIONAL JOURNAL OF FATIGUE, 2011, 33 (01) : 49 - 58
  • [43] Fretting-fatigue behaviour of bridge engineering cables in a solution of sodium chloride
    Perier, V.
    Dieng, L.
    Gaillet, L.
    Tessier, C.
    Fouvry, S.
    WEAR, 2009, 267 (1-4) : 308 - 314
  • [44] A fracture mechanics approach to interior fatigue crack growth in the very high cycle regime
    Ogawa, Takeshi
    Stanzl-Tschegg, Stefanie E.
    Schoenbauer, Bernd M.
    ENGINEERING FRACTURE MECHANICS, 2014, 115 : 241 - 254
  • [45] A review on fatigue fracture modes of structural metallic materials in very high cycle regime
    Sakai, Tatsuo
    Nakagawa, Akiyoshi
    Oguma, Noriyasu
    Nakamura, Yuki
    Ueno, Akira
    Kikuchi, Shoichi
    Sakaida, Akiyoshi
    INTERNATIONAL JOURNAL OF FATIGUE, 2016, 93 : 339 - 351
  • [46] Notch effect on fatigue strength reduction of bearing steel in the very high cycle regime
    Akiniwa, Yoshiaki
    Miyamoto, Nobuyuki
    Tsuru, Hirotaka
    Tanaka, Keisuke
    INTERNATIONAL JOURNAL OF FATIGUE, 2006, 28 (11) : 1555 - 1565
  • [47] Effects of nitrocarburizing on fatigue property of medium carbon steel in very high cycle regime
    Zhang, J. W.
    Lu, L. T.
    Shiozawa, K.
    Zhou, W. N.
    Zhang, W. H.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2011, 528 (22-23): : 7060 - 7067
  • [48] Very high cycle fatigue property of high-strength austempered ductile iron at conventional and ultrasonic frequency loading
    Zhang, Jiwang
    Song, Qingpeng
    Zhang, Ning
    Lu, Liantao
    Zhang, Mintang
    Cui, Guodong
    INTERNATIONAL JOURNAL OF FATIGUE, 2015, 70 : 235 - 240
  • [49] Fatigue of Austempered Ductile Iron with Two Strength Grades in Very High Cycle Regime
    Jiwang Zhang
    Wei Li
    Qingpeng Song
    Ning Zhang
    Liantao Lu
    Journal of Materials Engineering and Performance, 2016, 25 : 744 - 749
  • [50] Fatigue behavior and damage mechanism of a cast aluminum alloy in very high cycle regime
    Xue, Hongqian
    Bayraktar, E.
    Bathias, C.
    ADVANCES IN MATERIALS AND PROCESSING TECHNOLOGIES II, PTS 1 AND 2, 2011, 264-265 : 706 - +
12345