Inducing very high cycle fretting-fatigue in the ultrasonic regime

被引：11
|
作者：
Filgueiras, Pedro F. [2 ]
Bathias, Claude [1 ]
Palma, Ernani S. [2 ]
Wang, Chong [1 ]
机构：
[1] Univ Paris Ouest, Lab Energet Mecan Electromagnetisme, F-92410 Yule Davray, France
[2] Univ Fed Minas Gerais, Dept Mech Engn, BR-31270901 Belo Horizonte, MG, Brazil
来源：
TRIBOLOGY INTERNATIONAL | 2014年 / 76卷
关键词：
Fretting; Very high cycle fatigue; Ultrasonic testing; Fatigue damage; STEEL;
D O I：
10.1016/j.triboint.2013.10.023
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Early crack initiation due to fretting may have an important role in fatigue strength of steel components, mainly in the very high-cycle regime, i.e., beyond a million cycles. This work aimed to induce very high-cycle fretting-fatigue on a medium strength steel alloy in the ultrasonic regime. Specimens were subjected to push-pull fatigue and 10 mu m-amplitude fretting with crossed cylinders configuration. The normal load was held constant at 30 N. Results showed a knockdown factor of 1.5 for the fatigue strength in the fretting condition under study. The average diameter of the fretted surfaces was found to linearly increase with decreasing axial bulk stress amplitude. (C) 2014 Elsevier Ltd. All rights reserved.
引用
收藏
页码：57 / 62
页数：6
相关论文
共 50 条
  • [21] Effects of intermittent loading on fatigue life of a high strength steel in very high cycle fatigue regime
    Sun, Chengqi
    Song, Qingyuan
    Hu, Yuanpei
    Wei, Yujie
    INTERNATIONAL JOURNAL OF FATIGUE, 2018, 117 : 9 - 12
  • [22] Very high cycle fatigue testing of concrete using ultrasonic cycling
    Karr, Ulrike
    Schuller, Reinhard
    Fitzka, Michael
    Denk, Andreas
    Strauss, Alfred
    Mayer, Herwig
    MATERIALS TESTING, 2017, 59 (05) : 438 - 444
  • [23] Fatigue properties of oxynitrocarburized medium carbon railway axle steel in very high cycle regime
    Zhang, J. W.
    Lu, L. T.
    Shiozawa, K.
    Cui, G. D.
    Zhang, W. H.
    INTERNATIONAL JOURNAL OF FATIGUE, 2010, 32 (11) : 1805 - 1811
  • [24] Failure analysis of loom crankshafts in textile industry by fretting-fatigue
    Calderon-Hernandez, Jose Wilmar
    Perez-Giraldo, Mauricio
    Buitrago-Sierra, Robison
    Santa-Marin, Juan Felipe
    ENGINEERING FAILURE ANALYSIS, 2023, 151
  • [25] Effect of fretting damage on characteristics of high strength bearing steel up to very high cycle fatigue
    Huang, Zhiyong
    Zhang, Zhen
    Teng, Zhenjie
    Khan, Muhammad Kashif
    Wang, Qingyuan
    Wang, Jingyu
    ENGINEERING FRACTURE MECHANICS, 2019, 217
  • [26] On the formation of GBF of high-strength steels in the very high cycle fatigue regime
    Liu, Y. B.
    Yang, Z. G.
    Li, Y. D.
    Chen, S. M.
    Li, S. X.
    Hui, W. J.
    Weng, Y. Q.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 497 (1-2): : 408 - 415
  • [27] Fatigue Strength and Fracture Mechanisms in the Very-High-Cycle-Fatigue Regime of Automotive Steels
    Sadek, Mohamed
    Bergstrom, Jens
    Hallback, Nils
    Burman, Christer
    Elvira, Roberto
    Escauriaza, Borja
    STEEL RESEARCH INTERNATIONAL, 2020, 91 (08)
  • [28] On micro-defect induced cracking in very high cycle fatigue regime
    Zhu, Ming-Liang
    Zhu, Gang
    Xuan, Fu-Zhen
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2022, 45 (11) : 3393 - 3402
  • [29] Determination of fretting parameters of hoisting rope in coalmine and fretting-fatigue behavior of steel wires
    Wang, Dagang
    Zhang, Dekun
    Ge, Shirong
    INDUSTRIAL LUBRICATION AND TRIBOLOGY, 2013, 65 (06) : 436 - 448
  • [30] Influence of non-metallic inclusions on fatigue life in the very high cycle fatigue regime
    Krewerth, D.
    Lippmann, T.
    Weidner, A.
    Biermann, H.
    INTERNATIONAL JOURNAL OF FATIGUE, 2016, 84 : 40 - 52
12345