The mechanism for the high dependence of the Hall-Petch slope for twinning/slip on texture in Mg alloys

A Hall-Petch slope (k) that is highly changeable with texture, as extensively reported in Mg alloys, is ultimately related to the variation of deformation modes. In this paper, the influence of different (0002) distributions on k for twinning and slip was systematically studied using an AZ31 rolled plate ([0002]// ND) and extruded rod ([0002]LED together with a random distribution around the ED). The ND and ED refer to the normal direction of the plate and extrusion direction of the rod, respectively. A high dependency of k on the (0002) distribution is found, namely, a much lower k for {10T2} twinning in the plate (219 MPa mu m(1/2)) than that in the rod (435 MPa mu m(1/2)), but a much higher k for slip in the plate (437 MPa mu m(1/2)) than that in the rod (235 MPa mu m(1/2)). Compound use of the difference in Schmid factor (Delta SF) and geometric compatibility factor (m') quantitatively explains this orientation effect on k.Delta SF relates to the extra stress needed for the activation of slip/twinning in a neighboring grain, and m' reflects the efficiency of the stress concentration at the onset of slip/twinning in an adjacent grain. The lower m' for twinning in the rod versus the plate primarily accounts for the higher k for twinning in the rod. A much larger inclination of basal poles away from the ideal texture exists in the plate than in the rod, which induces a higher activity of basal slip during tension. The resultant high fraction of slip transfer from basal slip in one grain to prismatic slip in the neighboring grain largely amplifies Delta SF and reduces m', both of which yield a higher k for slip in the plate than in the rod. The relationship between the crystallographic orientation and m' was also calculated for different types of deformation transfer, and the main factor that determines m' was revealed. (C) 2017 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.