Crystallization of inorganic nonlinear optical zinc di-magnesium chloro sulphate (ZDMCS) single crystal

The growth of inorganic zinc di-magnesium chloro sulphate (ZDMCS) nonlinear optical material from low temperature evaporation technique at ambient temperature has been reported. The dimension of harvested crystal is 28x10x2 mm(3) and is possess rectangular shape morphology. The single crystal X-ray diffraction studies confirmed that the grown crystal belongs to the system of trigonal. The S-Cl stretching vibrations and Mg2+ ions present in the sample were observed by FTIR spectrometer. The cut-off wavelength of the grown crystal is about 203 nm is found by UV visible absorption spectrum. The nonlinear optical efficiency was determined by powder Kurtz Perry technique. EDAX spectrum confirms the presence of elements within the material. Dielectric nature of the sample was analyzed for the frequency range 50 Hz to 5 MHz at different temperatures. The mechanical behaviour of the title compound was investigated using Vicker's microhardness tester.