Impact of sodium excess on electrical conductivity of Na3Zr2Si2PO12 + x Na2O ceramics

被引:37
作者
Naqash, Sahir [1 ,2 ,3 ]
Tietz, Frank [1 ,2 ,3 ]
Yazhenskikh, Elena [2 ,4 ]
Mueller, Michael [2 ,4 ]
Guillon, Olivier [1 ,2 ,3 ]
机构
[1] Forschungszentrum Julich, Inst Energy & Climate Res, Mat Synth & Proc IEK 1, D-52425 Julich, Germany
[2] JARA Energy, Julich Aachen Res Alliance, Julich, Germany
[3] Forschungszentrum Julich, Helmholtz Inst Munster, D-52425 Julich, Germany
[4] Forschungszentrum Julich, Inst Energy & Climate Res, Microstruct & Properties Mat IEK 2, D-52425 Julich, Germany
关键词
IONIC-CONDUCTIVITY; CRYSTAL-STRUCTURE; TRANSPORT-PROPERTIES; NASICON; DIFFRACTION; ZIRCONIA; NA;
D O I
10.1016/j.ssi.2019.03.017
中图分类号
O64 [物理化学(理论化学)、化学物理学];
学科分类号
070304 ; 081704 ;
摘要
In order to industrialize NaSICON materials, modern fabrication techniques have to be used and one of those techniques for producing large-scale electrolyte sheets with 10-300 mu m thickness is tape casting. Such technique however requires a sintering step at high temperatures leading to sodium depletion due to evaporation. The sodium loss becomes more significant for large-area and thin components. In order to investigate and compensate the sodium loss, NaSICON compositions with sodium excess were prepared, i.e. Na3Zr2Si2PO12 + x Na2O (0 <= x <= 0.2). The sodium loss can be reduced by applying a two-step sintering process (1250 degrees C for only 0.5 h and then at 1230 degrees C for 5 h). Several characterization techniques were used to analyze the resulting ceramics, the sodium depletion and its consequence on electrical conductivity. Chemical analyses indicated that all compositions were sodium deficient. Furthermore, the weight loss was investigated by thermogravimetric analysis confirming the reduction of weight loss by a factor 2 by applying a two-step sintering procedure with lower second sintering temperature. Initial thermodynamic calculations of the phase equilibria at high temperatures confirm the predominant evaporation of sodium. The highest electrical conductivity (1.6 10(-3) S cm(-1) at 25 degrees C) was measured for the composition showing the least sodium deficiency (x = 0.2). Furthermore, the activation energy of bulk and grain boundary conductivity decreased with increasing x in system.
引用
收藏
页码:57 / 66
页数:10
相关论文
共 43 条
[1]   DEPENDENCE OF THE PROPERTIES OF NASICONS ON THEIR COMPOSITION AND PROCESSING [J].
AHMAD, A ;
WHEAT, TA ;
KURIAKOSE, AK ;
CANADAY, JD ;
MCDONALD, AG .
SOLID STATE IONICS, 1987, 24 (01) :89-97
[2]   A wide-ranging review on Nasicon type materials [J].
Anantharamulu, N. ;
Rao, K. Koteswara ;
Rambabu, G. ;
Kumar, B. Vijaya ;
Radha, Velchuri ;
Vithal, M. .
JOURNAL OF MATERIALS SCIENCE, 2011, 46 (09) :2821-2837
[3]  
[Anonymous], 1979, P INT C FAST ION TRA
[4]   FactSage thermochemical software and databases, 2010-2016 [J].
Bale, C. W. ;
Belisle, E. ;
Chartrand, P. ;
Decterov, S. A. ;
Eriksson, G. ;
Gheribi, A. E. ;
Hack, K. ;
Jung, I. -H. ;
Kang, Y. -B. ;
Melancon, J. ;
Pelton, A. D. ;
Petersen, S. ;
Robelin, C. ;
Sangster, J. ;
Spencer, P. ;
Van Ende, M-A. .
CALPHAD-COMPUTER COUPLING OF PHASE DIAGRAMS AND THERMOCHEMISTRY, 2016, 54 :35-53
[5]   NEUTRON POWDER DIFFRACTION STUDY AND IONIC-CONDUCTIVITY OF NA2ZR2SIP2O12 AND NA3ZR2SI2PO12 [J].
BAUR, WH ;
DYGAS, JR ;
WHITMORE, DH ;
FABER, J .
SOLID STATE IONICS, 1986, 18-9 :935-943
[6]   NASICON - AMORPHOUS TO CRYSTALLINE COMPOUNDS [J].
BOILOT, JP ;
COLOMBAN, P ;
COLLIN, G .
SOLID STATE IONICS, 1986, 18-9 (pt 2) :974-980
[7]   Lithium location in NASICON-type Li+ conductors by neutron diffraction.: I.: Triclinic α′-LiZr2(PO4)3 [J].
Catti, M ;
Stramare, S ;
Ibberson, R .
SOLID STATE IONICS, 1999, 123 (1-4) :173-180
[8]  
Chatterjee S., 2018, P AIP C AM I PHYS
[9]   Sintering dense nanocrystalline ceramics without final-stage grain growth [J].
Chen, IW ;
Wang, XH .
NATURE, 2000, 404 (6774) :168-171
[10]  
Feng P., 2014, SCI REP, V4, P10