INTERNAL FRICTION PEAK IN B2 Fe-Al ALLOYS DURING ORDERING PROCESS

被引:0
作者
Wu Jie [1 ]
Cui Hongzhi [1 ]
Chi Jing [1 ]
Yao Shuyu [1 ]
Han Fusheng [2 ]
机构
[1] Shandong Univ Sci & Technol, Coll Mat Sci & Engn, Qingdao 266510, Peoples R China
[2] Chinese Acad Sci, Inst Solid State Phys, Key Lab Mat Phys, Hefei 230031, Peoples R China
关键词
B2 Fe-Al alloy; internal friction; degree of order; antisite atom; INTERMETALLIC COMPOUND FEAL; DISORDER TRANSFORMATION; DAMPING BEHAVIOR; RELAXATION; TRANSITION; KINETICS;
D O I
暂无
中图分类号
TF [冶金工业];
学科分类号
0806 ;
摘要
The internal friction behaviors of B2 Fe-Al alloys were examined to understand the correlation between the ordering process and the atomic movement. An internal friction peak was found at around 570 degrees C in the oil-cooled Fe47Al53 alloy, while the peak in the furnace-cooled specimens disappeared. The peak has the typical phase transition character. Combined with analyses of XRD and DSC, it is proposed that the peak originates from the ordering process, which is caused by the jump of antisite atoms to their own sublattice sites through the nearest neighboring vacancies. Similar internal peak was observed also at 540 degrees C for Fe57Al43 alloy.
引用
收藏
页码:396 / 399
页数:4
相关论文
共 19 条
[1]   Study of the weight of different contributions to the magnetic reinforcement in the order-disorder transition of FeAl alloys [J].
Apiñaniz, E ;
Plazaola, F ;
Garitaonandia, JS .
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2004, 272 :794-796
[2]   The anti-structural bridge mechanism for diffusion in ordered alloys of the B2 type [J].
Belova, IV ;
Murch, GE .
INTERMETALLICS, 1998, 6 (02) :115-119
[3]   Lattice parameter dependence on long-range ordered degree during order-disorder transformation [J].
Chen, GL ;
Ni, XD ;
Nsongo, T .
INTERMETALLICS, 2004, 12 (7-9) :733-739
[4]   ORIGIN OF ORDERING IN B2-TYPE TRANSITION-METAL ALUMINIDES - COMPARATIVE-STUDY OF THE DEFECT PROPERTIES OF PDAL, NIAL, AND FEAL [J].
FU, CL .
PHYSICAL REVIEW B, 1995, 52 (05) :3151-3158
[5]   The effect of electronic structure on the defect properties of FeAl [J].
Fu, CL ;
Wang, XD .
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 240 :761-768
[6]   Damping behavior of foamed aluminum [J].
Han, FS ;
Zhu, ZG ;
Liu, CS ;
Gao, JC .
METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1999, 30 (03) :771-776
[7]   Vacancy clustering and relaxation behavior in rapidly solidified B2FeAl ribbons [J].
Haraguchi, T ;
Yoshimi, K ;
Yoo, MH ;
Kato, H ;
Hanada, S ;
Inoue, A .
ACTA MATERIALIA, 2005, 53 (13) :3751-3764
[8]   REACTION KINETICS IN DIFFERENTIAL THERMAL ANALYSIS [J].
KISSINGER, HE .
ANALYTICAL CHEMISTRY, 1957, 29 (11) :1702-1706
[9]   Point defect behavior in high temperature region in the B2-type intermetallic compound FeAl [J].
Kogachi, M ;
Haraguchi, T ;
Kim, SM .
INTERMETALLICS, 1998, 6 (06) :499-510
[10]   Random vacancy distribution in B2-type intermetallic compound FeAl [J].
Kogachi, M ;
Haraguchi, T .
SCRIPTA MATERIALIA, 1998, 39 (02) :159-165