Multi-wire metallization for solar cells: Contact resistivity of the interface between the wires and In2O3:Sn, In2O3:F, and ZnO:Al layers

被引:17
作者
Untila, G. G. [1 ]
Kost, T. N. [1 ]
Chebotareva, A. B. [1 ]
机构
[1] Lomonosov Moscow State Univ, Skobeltsyn Inst Nucl Phys, Moscow 119991, Russia
基金
俄罗斯基础研究基金会;
关键词
Silicon solar cells; Transparent conductive oxide; Metallization; Multi-wire design; Ag/cost reduction; Specific contact resistance; Transmission line method; ULTRASONIC SPRAY-PYROLYSIS; HOLE-SELECTIVE CONTACTS; INDIUM OXIDE-FILMS; TIN OXIDE; SILICON; EFFICIENCY; OPTIMIZATION; RESISTANCE; ELECTRODES; PASSIVATION;
D O I
10.1016/j.solener.2016.12.049
中图分类号
TE [石油、天然气工业]; TK [能源与动力工程];
学科分类号
0807 ; 0820 ;
摘要
Replacing expensive silver with inexpensive copper for the metallization of silicon wafer solar cells can lead to substantial reductions in material costs associated with cell production. A promising approach is the use of multi-wire design. This technology uses many wires in the place of busbars, and the copper wires are "soldered" during the low-temperature lamination process to the fingers (printed or plated) or to the transparent conductive oxide (TCO) layer, e.g. in the case of the alpha-Si/c-Si heterojunction cells. We have studied the effects of Si surface morphology (textured or planar) and TCO resistivity (rho) on the contact resistivity (rho(c)) between wires and TCO (In2O3:Sn (ITO), In2O3:F (IFO), and ZnO:Al (AZO)) layers grown on silicon substrates by ultrasonic spray pyrolysis. To determine pc by transmission line model (TLM) measurements, we have developed a specialized TLM test structure which takes into account specifics of laminated contacts. It has been shown that, if the longitudinal resistance of the wires is left out of account, the error in pc determined by TLM measurements may reach tens or hundreds of percent or even more. To eliminate such errors, we have adjusted the TLM measurement procedure. The present results demonstrate the following: (i) In all the groups of our samples, rho(c) increases with rho and the rho(c)(rho) data can be represented by a power-law trend line. (ii) For ITO and IFO, pc is lower in the case of a textured surface: 0.3-6 m Omega cm(2) at rho = 0.2-3 m Omega cm. (iii) In contrast, for the AZO films rho(c) is lower in the case of a planar Si surface: 5-140 m Omega cm(2) at rho = 9-80 m Omega cm. These findings have been used to analyze the series resistance (R-s) of AZO/n-Si heterojunction solar cells. The contribution of rho(c) to R-s has been shown to reach 30-40%. (C) 2016 Elsevier Ltd. All rights reserved.
引用
收藏
页码:330 / 339
页数:10
相关论文
共 44 条
[31]   Specific contact resistances between amorphous oxide semiconductor In-Ga-Zn-O and metallic electrodes [J].
Shimura, Yasuhiro ;
Nomura, Kenji ;
Yanagi, Hiroshi ;
Kamiya, Toshio ;
Hirano, Masahiro ;
Hosono, Hideo .
THIN SOLID FILMS, 2008, 516 (17) :5899-5902
[32]   Improving low pressure chemical vapor deposited zinc oxide contacts for thin film silicon solar cells by using rough glass substrates [J].
Steinhauser, J. ;
Boucher, J. -F. ;
Omnes, E. ;
Borrello, D. ;
Vallat-Sauvain, E. ;
Monteduro, G. ;
Marmelo, M. ;
Orhan, J. -B. ;
Wolf, B. ;
Bailat, J. ;
Benagli, S. ;
Meier, J. ;
Kroll, U. .
THIN SOLID FILMS, 2011, 520 (04) :1218-1222
[33]   Natural resource limitations to terawatt-scale solar cells [J].
Tao, Coby S. ;
Jiang, Jiechao ;
Tao, Meng .
SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2011, 95 (12) :3176-3180
[34]  
Untila G., 2001, P 17 EUR PHOT SOL EN, P1793
[35]   Bifacial 8.3%/5.4% front/rear efficiency ZnO:Al/n-Si heterojunction solar cell produced by spray pyrolysis [J].
Untila, G. G. ;
Kost, T. N. ;
Chebotareva, A. B. .
SOLAR ENERGY, 2016, 127 :184-197
[36]   Contact resistance of indium tin oxide and fluorine-doped indium oxide films grown by ultrasonic spray pyrolysis to diffusion layers in silicon solar cells [J].
Untila, G. G. ;
Kost, T. N. ;
Chebotareva, A. B. ;
Kireeva, E. D. .
SOLAR ENERGY MATERIALS AND SOLAR CELLS, 2015, 137 :26-33
[37]   Pyrosol-deposited Ga-doped ZnO (GZO) transparent electrodes in GZO/(p+nn+)c-Si solar cells [J].
Untila, G. G. ;
Kost, T. N. ;
Chebotareva, A. B. ;
Zuev, D. A. ;
Stepanov, A. S. ;
Shevaleevskiy, O. I. .
VACUUM, 2015, 114 :188-197
[38]   Concentrator bifacial Ag-free LGCells [J].
Untila, G. G. ;
Kost, T. N. ;
Chebotareva, A. B. ;
Zaks, M. B. ;
Sitnikov, A. M. ;
Solodukha, O. I. ;
Shvarts, M. Z. .
SOLAR ENERGY, 2014, 106 :88-94
[39]   Passivation of boron-doped p+-Si emitters in the (p+nn+)Si solar cell structure with AlOx grown by ultrasonic spray pyrolysis [J].
Untila, G. G. ;
Kost, T. N. ;
Chebotareva, A. B. ;
Stepanov, A. S. ;
Zaks, M. B. ;
Sitnikov, A. M. ;
Solodukha, O. I. .
SOLAR ENERGY, 2013, 98 :440-447
[40]   Optimization of the deposition and annealing conditions of fluorine-doped indium oxide films for silicon solar cells [J].
Untila, G. G. ;
Kost, T. N. ;
Chebotareva, A. B. ;
Timofeyev, M. A. .
SEMICONDUCTORS, 2013, 47 (03) :415-421