Preparation and performance of the modified high-strength/high-modulus polyvinyl alcohol fiber/polyurethane grouting materials

被引：45

作者：

Cao, Ming ^{[1
]}

Wang, Chuanyong ^{[1
]}

Xia, Ru ^{[1
]}

Chen, Peng ^{[1
]}

Miao, Jibin ^{[1
]}

Yang, Bin ^{[1
]}

Qian, Jiasheng ^{[1
]}

Tang, Yongzhi ^{[2
]}

机构：

[1] Anhui Univ, Key Lab Environm Friendly Polymer Mat Anhui Pro, Sch Chem & Chem Engn, Hefei 230601, Anhui, Peoples R China

[2] Huainan Min Grp Co Ltd, Huainan 232001, Anhui, Peoples R China

来源：

CONSTRUCTION AND BUILDING MATERIALS | 2018年 / 168卷

基金：

中国国家自然科学基金;

关键词：

PVA Fibre; Grouting materials; Adhesion; Mechanical properties; MECHANICAL-PROPERTIES; POLYURETHANE COMPOSITES; CARBON-FIBER; PVA FIBER; NANOCOMPOSITES; SURFACE; MONTMORILLONITE; NANOPARTICLES; GEOPOLYMER; CLAY;

D O I：

10.1016/j.conbuildmat.2018.02.173

中图分类号：

TU [建筑科学];

学科分类号：

0813 ;

摘要：

In this study, modified polyvinyl alcohol fiber (MPVA) filled polyurethane (MPVA/PU) grouting materials with high interfacial bonding strength were prepared. Firstly, the high-strength/high-modulus PVA fibers were modified by gamma-aminopropyl triethoxysilane (APTES) and diphenyl-methane-diisocyanate (MDI) respectively. The chemical structure, surface morphology and hydrophilicity were characterized by FT-IR,XPS, SEM and contact angle analysis. Second, the performance of PU mixed with different dosages of modified PVA fibers as the grouting material was studied. The results showed that mechanical properties and hot air aging resistance of the MPVA/PU composite were significantly increased compared with pure PU. In particular, it also can be found that modified PVA fiber bring better interface adhesion, especially, when the dosage is 0.1%, the best overall performance of MPVA/PU can be achieved. SEM analysis demonstrated that the interface adhesion between modified PVA fiber and PU was obviously improved. (C) 2018 Elsevier Ltd. All rights reserved.

引用

页码：482 / 489

页数：8

共 37 条

[1] Strain hardening behavior of lightweight hybrid polyvinyl alcohol (PVA) fiber reinforced cement composites [J].

Ahmed, Shaikh Faiz Uddin ;

Mihashi, Hirozo .

MATERIALS AND STRUCTURES, 2011, 44 (06) :1179-1191

[2] Effect of different superplasticisers on the physical and mechanical properties of cement grouts [J].

Anagnostopoulos, Costas A. .

CONSTRUCTION AND BUILDING MATERIALS, 2014, 50 :162-168

[3] Strengthening of brick masonry with PVA fiber reinforced cement stucco [J].

Arisoy, Bengi ;

Ercan, Emre ;

Demir, Ali .

CONSTRUCTION AND BUILDING MATERIALS, 2015, 79 :255-262

[4] Preparation of scratch and abrasion resistant polymeric nanocomposites by monomer grafting onto nanoparticles, 5a -: Application of mass Spectroscopy and atomic force microscopy to the characterization of silane-modified silica surface [J].

Bauer, F ;

Ernst, H ;

Hirsch, D ;

Naumov, S ;

Pelzing, M ;

Sauerland, V ;

Mehnert, R .

MACROMOLECULAR CHEMISTRY AND PHYSICS, 2004, 205 (12) :1587-1593

[5] Silica sol for rock grouting: Laboratory testing of strength, fracture behaviour and hydraulic conductivity [J].

Butron, Christian ;

Axelsson, Magnus ;

Gustafson, Gunnar .

TUNNELLING AND UNDERGROUND SPACE TECHNOLOGY, 2009, 24 (06) :603-607

[6]

Canakci H., 2017, ARAB J SCI ENG, V3, P1

[7] Damping, thermal, and mechanical properties of montmorillonite modified castor oil-based polyurethane/epoxy graft IPN composites [J].

Chen, Shoubing ;

Wang, Qihua ;

Wang, Tingmei .

MATERIALS CHEMISTRY AND PHYSICS, 2011, 130 (1-2) :680-684

[8] The surface modification of TiN nano-particles using macromolecular coupling agents, and their resulting dispersibility [J].

Cheng, Guojun ;

Qian, Jiasheng ;

Miao, Jibin ;

Yang, Bin ;

Xia, Ru ;

Chen, Peng .

APPLIED SURFACE SCIENCE, 2014, 301 :79-84

[9] On the viscous behavior of cement mixtures with clay, sand, lime and bottom ash for jet grouting [J].

Gullu, Hamza .

CONSTRUCTION AND BUILDING MATERIALS, 2015, 93 :891-910

[10]

Guo H., 2014, POLYURETHANE IND, V29, P46

← 1 2 3 4 →